Resist composition and method for producing resist pattern

ABSTRACT

A resist composition containing; (A1) a resin having a structural unit represented by the formula (I), (A2) a resin being insoluble or poorly soluble in alkali aqueous solution, but becoming soluble in an alkali aqueous solution by the action of an acid, (B) an acid generator, and (D) a salt having an anion represented by the formula (IA), 
     
       
         
         
             
             
         
       
         
         
           
             wherein R 1 , A 1 , R 2 , R 1A  and R 2A  are defined in the specification.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to Japanese Application No. 2011-39450 filed on Feb. 25, 2011. The entire disclosures of Japanese Application No. 2011-39450 is incorporated hereinto by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a resist composition and a method for producing resist pattern.

2. Background Information

A resist composition which contains a resin having a polymer obtained by polymerizing a compound represented by the formula (u-A) and a compound represented by the formula (u-B), and a polymer obtained by polymerizing a compound represented by the formula (u-B), a compound represented by the formula (u-C) and a compound represented by the formula (u-D); an acid generator; and a solvent, is described in Patent document of JP-2010-197413A.

However, with the conventional resist composition, the focus margin (DOF) at producing a resist pattern may be not always satisfied with, and number of the defects of the resist pattern to be produced from the resist composition may quite increase.

SUMMARY OF THE INVENTION

The present invention provides following inventions of <1> to <6>.

<1> A resist composition having;

(A1) a resin having a structural unit represented by the formula (I),

(A2) a resin being insoluble or poorly soluble in alkali aqueous solution, but becoming soluble in an alkali aqueous solution by the action of an acid,

(B) an acid generator, and

(D) a salt having an anion represented by the formula (IA).

wherein R¹ represents a hydrogen atom or a methyl group;

A¹ represents a C₁ to C₆ alkanediyl group;

R² represents a C₁ to C₁₀ hydrocarbon group having a fluorine atom.

wherein R^(1A) and R^(2A) independently represent a hydrogen atom, a C₁ to C₁₂ aliphatic hydrocarbon group, a C₃ to C₂₀ alicyclic hydrocarbon group, a C₆ to C₂₀ aromatic hydrocarbon group or a C₇ to C₂₁ aralkyl group, one or more hydrogen atom contained in the aliphatic hydrocarbon, the alicyclic hydrocarbon group, the aromatic hydrocarbon group and the aralkyl group may be replaced by a hydroxy group, a cyano group, a fluorine atom, a trifluoromethyl group or a nitro group, and one or more —CH₂— contained in the aliphatic hydrocarbon group may be replaced by —O— or —CO—, or R^(1A) and R^(2A) may be bonded together with a nitrogen atom bonded thereto to form a C₄ to C₂₀ ring.

<2> The resist composition according to <1>, wherein R² in the formula (I) is a C₁ to C₆ fluorinated alkyl group.

<3> The resist composition according to <1> or <2>, wherein A¹ in the formula (I) is a C₂ to C₄ alkanediyl group.

<4> The resist composition according to any one of <1> to <3>, wherein A¹ in the formula (I) is an ethylene group.

<5> The resist composition according to any one of <1> to <4>, wherein the salt having an anion represented by the formula (IA) contains a cation represented by the formula (IB).

wherein R³, R⁴ and R⁵ in each occurrence independently represent a hydroxy group, a halogen atom, a C₁ to C₁₂ alkyl group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₁ to C₁₂ alkoxy group, and the alkyl group, the alicyclic hydrocarbon group and the alkoxy group may be substituted with a halogen group, a hydroxy group, a C₁ to C₁₂ alkoxy group, a C₆ to C₁₈ aromatic hydrocarbon group, a C₂ to C₄ acyl group or a glycidyloxy group;

mx to m/z independently represent an integer of 0 to 5.

<6> The resist composition according to any one of <1> to <5>, which further comprises a solvent.

<7> A method for producing resist pattern comprising steps of;

(1) applying the resist composition of any one of <1> to <6> onto a substrate;

(2) drying the applied composition to form a composition layer;

(3) exposing the composition layer;

(4) heating the exposed composition layer, and

(5) developing the heated composition layer.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

“(Meth)acrylic monomer” means at least one monomer having a structure of “CH₂═CH—CO—” or “CH₂═C(CH₃)—CO—”, as well as “(meth)acrylate” and “(meth)acrylic acid” mean “at least one acrylate or methacrylate” and “at least one acrylic acid or methacrylic acid,” respectively.

<Resist Composition>

The resist composition of the present invention contains;

(A) a resin (hereinafter may be referred to as “resin (A)”),

(B) an acid generator (hereinafter may be referred to as “acid generator (B)”), and

(D) a salt having an anion represented by the formula (IA) (hereinafter may be referred to as “salt (IA)”).

Further, the present resist composition preferably contains a solvent (hereinafter may be referred to as “solvent (E)”), as needed.

<Resin (A)>

The resin (A) includes;

(A1) a resin having a structural unit represented by the formula (I), and

(A2) a resin being insoluble or poorly soluble in alkali aqueous solution, but becoming soluble in an alkali aqueous solution by the action of an acid.

Also, the resin (A) may contain a structural unit other than the resin (A1) and resin (A2).

<Resin (A1)>

The resin (A1) has a structural unit represented by the formula (I) (hereinafter may be referred to as “structural unit (I)”).

wherein R¹ represents a hydrogen atom or a methyl group;

A¹ represents a C₁ to C₆ alkanediyl group;

R² represents a C₁ to C₁₀ hydrocarbon group having a fluorine atom.

In the formula (I), examples of the alkanediyl of A¹ group include a chain alkanediyl group such as methylene, ethylene, propane-1,3-diyl, propane-1,2-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl; a branched alkanediyl group such as 1-methylpropane-1,3-diyl, 2-methylpropane-1,3-diyl, 2-methylpropane-1,2-diyl, 1-methylbutane-1,4-diyl, 2-methylbutane-1,4-diyl groups.

The hydrocarbon group of R² may be any of an aliphatic hydrocarbon group, an aromatic hydrocarbon group and a combination of two or more such groups. The aliphatic hydrocarbon group may be any of a chain and cyclic aliphatic hydrocarbon group, and a combination of two or more such groups. The aliphatic hydrocarbon group is preferably an alkyl group and an alicyclic group.

Examples of the alkyl group include methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, text-butyl, n-pentyl, iso-pentyl, tert-pentyl, neo-pentyl, hexyl, octyl and 2-ethylhexyl groups.

The alicyclic hydrocarbon group may be either monocyclic or polycyclic hydrocarbon group. Examples of the monocyclic alicyclic hydrocarbon group include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, methylcyclohexyl, dimethylcyclohexyl, cycloheptyl, cyclooctyl and cyclodecyl groups. Examples of the polycyclic alicyclic hydrocarbon group include decahydronaphtyl, adamantyl, 2-alkyladamantane-2-yl, 1-(adamantane-1-yl)alkane-1-yl, norbornyl, methylnorbornyl and isobornyl groups.

The hydrocarbon group having a fluorine atom of R² is preferably an alkyl group having a fluorine atom and an alicyclic hydrocarbon group having a fluorine atom.

Examples of the alkyl group having a fluorine atom include a fluorinated alkyl group such as difluoromethyl, trifluoromethyl, 1,1-difluoroethyl, 2,2-difluoroethyl, 1,1,1-trifluoroethyl, 2,2,2-trifluoroethyl, perfluoroethyl, 1,1,2,2-tetrafluoropropyl, 1,1,1,2,2-pentafluoropropyl, 1,1,2,2,3,3-hexafluoropropyl, perfluoroethylmethyl, 1-(trifluoromethyl)-1,2,2,2-tetratrifluoroethyl, perfluoropropyl, 1,1,2,2-tetrafluorobutyl, 1,1,2,2,3,3-hexafluorobutyl, 1,1,2,2,3,3,4,4-octafluorobutyl, perfluorobutyl, 1,1-bis(trifluoro)methyl-2,2,2-trifluoroethyl, 2-(perfluoropropyl)ethyl, 1,1,2,2,3,3,4,4-octafluoropentyl, 1,1,1,2,2,3,3,4,4-nonafluoropentyl, perfluoropentyl, 1,1,2,2,3,3,4,4,5,5-decafluoropentyl, 1,1-bis(trifluoromethyl)-2,2,3,3,3-pentafluoropropyl, 1,1,1,2,2,3,3,4,4-nonafluoropentyl, perfluoropentyl, 2-(perfluorobutyl)ethyl, 1,1,2,2,3,3,4,4,5,5-decafluorohexyl, 1,1,2,2,3,3,4,4,5,5,6,6-dodecafluorohexyl, perfluoropentylmethyl, perfluorohexyl, perfluoroheptyl and perfluorooctyl groups.

Examples of the alicyclic haydrocarbon group having a fluorine atom include a fluorinated cycloalkyl group such as perfluoricyclohexyl and perfluoroadamanthyl groups.

A¹ in the formula (I) is preferably a C₂ to C₄ alkanediyl group, and more preferably an ethylene group.

R² is preferably a fluorinated alkyl group, and more preferably a C₁ to C₆ fluorinated alkyl group.

Specific examples of the structural units (I) include as follows.

Also, examples of the structural units (I) include structural units in which a methyl group corresponding to R¹ in the structural units represented by the above is replaced by a hydrogen atom.

The structural unit (I) is derived from a compound represented by the formula (I′), hereinafter may be referred to as “compound (I′)”.

wherein A¹, R¹ and R² have the same definition of the above.

The compound (I′) can be produced by a method below.

wherein A¹, R¹ and R² have the same definition of the above.

The compound (I′) can be obtained by reacting a compound represented by the formula (I′-1) with a compound represented by the formula (I′-2) in presence of a basic catalyst in a solvent. Preferred examples of the basic catalyst include pyridine. Preferred examples of the solvent include tetrahydrofuran.

As the compound represented by the formula (I′-1), a marketed product may be used. The hydroxyethyl methacrylate can be used as a marketed product.

The compound represented by the formula (I′-2) can be obtained by converting corresponding carboxylic acid, depending on the kinds of R², into an anhydride. The heptafluoro butyric anhydride can be used as a marketed product.

The resin (A1) may include a structural unit other than the structural unit (I).

Examples of the structural unit other than the structural unit (I) include a structural unit derived from a monomer having an acid labile group described below (hereinafter may be referred to as “acid labile monomer (a1)”), a structural unit derived from a monomer not having an acid labile group described below (hereinafter may be referred to as “acid stable monomer”), a structural unit derived from a known monomer in this field, a structural unit represented by the formula (MA) described below. Among these, a structural unit represented by the formula (IIIA) is preferable.

wherein R¹¹ represents a hydrogen atom or a methyl group;

ring W² represents a C₆ to C₁₀ hydrocarbon ring; A¹² represents —O—, *—CO—O— or *—O—CO—, * represents a bond to ring W²;

R¹² represents a C₁ to C₆ hydrocarbon group having a fluorine atom.

The hydrocarbon ring of W² may be an alicyclic hydrocarbon ring, and preferably a saturated alicyclic hydrocarbon ring.

Examples of the saturated alicyclic hydrocarbon ring include a ring below.

As the ring W², an adamantane ring and cyclohexane ring are preferable, and an adamantane ring is more preferable.

Examples of the R² include a group below.

Examples of the structural unit represented by the formula (IIIA) include structural units below.

Also, examples of the structural units (IIIA) include structural units in which a methyl group corresponding to R¹¹ in the structural units represented by the above is replaced by a hydrogen atom.

Among these, the structural unit (IIIA-1) and the structural unit (IIIA-1) in which a methyl group corresponding to R¹¹ in the structural units represented by the above is replaced by a hydrogen atom are preferable.

The proportion of the structural unit (I) in the resin (A1) is generally 5 to 100 mol %, preferably 10 to 100 mol %, more preferably 50 to 100 mol %, still more preferably 80 to 100 mol %, and, in particular, preferably almost 100 mol %, with respect to the total structural units (100 mol %) constituting the resin (A1).

Within the proportion of the structural unit (I), it is possible to produce a resist pattern with excellent wide focus margin (DOF) and few defects.

When the resin (A1) contains the structural unit (IIIA), the proportion thereof in the resin (A1) is generally 1 to 95 mol %, preferably 2 to 80 mol %, more preferably 5 to 70 mol %, still more preferably 5 to 50 mol %, and particularly preferably 5 to 30 mol %, with respect to the total structural units (100 mol %) constituting the resin (A1).

For achieving the proportion of the structural unit (I) and/or the structural unit (IIIA) in the resin (A1) within the above range, the amount of the compound (P) and/or a monomer giving the structural unit (IIIA) to be used can be adjusted with respect to the total amount of the monomer to be used when the resin (A1) is produced (the same shall apply hereinafter for corresponding adjustment of the proportion).

The resin (A1) can be produced by a known polymerization method, for example, radical polymerization method, using at least one of the compound (I′) and/or at least one of the monomer giving the structural unit (IIIA), and optionally at least one of the acid labile monomer (a1), least one of the acid stable monomer and/or at least one of a known compound.

The weight average molecular weight of the resin (A) is preferably 5,000 or more (more preferably 7,000 or more, and still more preferably 10,000 or more), and 80,000 or less (more preferably 50,000 or less, and still more preferably 30,000 or less).

The weight average molecular weight is a value determined by gel permeation chromatography using polystyrene as the standard product. The detailed condition of this analysis is described in Examples.

<Resin (A2)>

The resin (A2) is a resin having properties which is insoluble or poorly soluble in alkali aqueous solution, but becomes soluble in an alkali aqueous solution by the action of an acid, Here “becomes soluble in an alkali aqueous solution by the action of an acid” means a resin that is insoluble or poorly soluble in aqueous alkali solution before contact with the acid, and becomes soluble in aqueous alkali solution after contact with an acid.

Therefore, the resin (A2) is preferably a resin having at least one of the structural unit derived from an acid labile monomer (a1) described below.

Also, the resin (A2) may include a structural unit other than the structural unit having the acid labile group as long as the resin (A2) has above properties.

Examples of the structural unit other than the structural unit having the acid labile group include a structural unit derived from the acid stable monomer, the structural unit derived from a known monomer in this field, the structural units represented by the formula (I) and the formula (IIIA) described above.

The resin (A2) may be a different resin from the resin (A1), or a resin which has the structural unit represented by the formula (I) and/or the formula (IIIA) described above so long as the resin (A2) has properties which is insoluble or poorly soluble in alkali aqueous solution, but becomes soluble in an alkali aqueous solution by the action of an acid.

<Acid Labile Monomer (a1)>

The “acid labile group” means a group which has an elimination group and in which the elimination group is detached by contacting with an acid resulting in forming a hydrophilic group such as a hydroxy or carboxy group. Examples of the acid labile group include a group represented by the formula (1) and a group represented by the formula (2). Hereinafter a group represented by the formula (1) may refer to as an “acid labile group (1), and a group represented by the formula (2) may refer to as an “acid labile group (2).

wherein R^(a1) to R^(a3) independently represent a C₁ to C₈ alkyl group or a C₃ to C₂₀ alicyclic hydrocarbon group, or R^(a1) and R^(a2) may be bonded together to form a C₂ to C₂₀ divalent hydrocarbon group, * represents a bond. In particular, the bond here represents a bonding site (the similar shall apply hereinafter for “bond”).

wherein R^(a1′) and R^(a2′) independently represent a hydrogen atom or a C₁ to C₁₂ hydrocarbon group, R^(a3′) represents a C₂ to C₂₀ hydrocarbon group, or R^(a2′) and R^(a3′) may be bonded together to form a C₂ to C₂₀ divalent hydrocarbon group, and one or more —CH₂— contained in the hydrocarbon group or the divalent hydrocarbon group may be replaced by —O— or —S—, * represents a bond.

Examples of the alkyl group of R^(a1) to R^(a3) include methyl, ethyl, propyl, butyl, pentyl and hexyl groups.

Examples of the alicyclic hydrocarbon group of R^(a1) to R^(a3) include monocyclic groups such as cyclopentyl, cyclohexyl, methylcyclohexyl, dimethylcyclohexyl, cycloheptyl, cyclooctyl groups; and polycyclic hydrocarbon groups such as decahydronaphtyl, adamantyl, norbornyl (i.e., bicyclo[2.2.1]hexyl), and methyl norbornyl groups as well as groups below.

The alicyclic hydrocarbon group of R^(a1) and R^(a2) preferably has 3 to 16 carbon atoms.

When R^(a1) and R^(a2) is bonded together to form a C₂ to C₂₀ hydrocarbon group, examples of the group-C(R^(a1))(R^(a2))(R^(a3)) include groups below. The divalent hydrocarbon group preferably has 3 to 12 carbon atoms.

Specific examples of the acid labile group (1) include, for example,

1,1-dialkylalkoxycarbonyl group (a group in which R^(a1) to R^(a3) are alkyl groups, preferably tert-butoxycarbonyl group, in the formula (1)),

2-alkyladamantane-2-yloxycarbonyl group (a group in which R^(a1), R^(a2) and a carbon atom form adamantyl group, and R^(a3) is alkyl group, in the formula (1)), and

1-(adamantine-1-yl)-1-alkylalkoxycarbonyl group (a group in which R^(a1) and R^(a2) are alkyl group, and R^(a3) is adamantyl group, in the formula (1)).

The hydrocarbon group of R^(a1′) to R^(a3′) includes any of an alkyl group, an alicyclic hydrocarbon group and an aromatic hydrocarbon group.

Examples of the aromatic hydrocarbon group include an aryl group such as phenyl, naphthyl, anthryl, p-methylphenyl, p-tert-butylphenyl, p-adamantylphenyl, tolyl, xylyl, cumenyl, mesityl, biphenyl, phenanthryl, 2,6-diethylphenyl and 2-methyl-6-ethylphenyl groups.

Examples of the divalent hydrocarbon group which is formed by bonding with R^(a2′) and R^(a3′) include groups in which a hydrogen atom in the hydrocarbon group of R² of the formula (I) is removed.

At least one of R^(a1′) and R^(a2′) is preferably a hydrogen atom.

Specific examples of the acid labile group (2) include a group below.

The acid labile monomer (a1) is preferably a monomer having an acid labile group and a carbon-carbon double bond, and more preferably a (meth)acrylic monomer having the acid labile group.

Among the (meth)acrylic monomer having an acid labile group, it is preferably a monomer having a C₅ to C₂₀ alicyclic hydrocarbon group. When a resin which can be obtained by polymerizing monomers having bulky structure such as the alicyclic hydrocarbon group is used, the resist composition having excellent resolution tends to be obtained during the production of a resist pattern.

Examples of the (meth)acrylic monomer having the acid labile group and a carbon-carbon double bond preferably include a monomer represented by the formula (a1-1) and a monomer represented by the formula (a1-2), below (hereinafter may be referred to as a “monomer (a1-1)” and a “monomer (a1-2)”). These may be used as a single monomer or as a combination of two or more monomers. The monomer (a1-1) induces a structural unit represented by the formula (a1-1), and the monomer (a1-2) induces a structural unit represented by the formula (a1-2) as described below (hereinafter may be referred to as the “structural unit (a1-1)” and the “structural unit (a1-2)”).

wherein L^(a1) and L^(a2) independently represent *—O— or *—O—(CH₂)_(k1)—CO—O—, k1 represents an integer of 1 to 7, * represents a bond to the carbonyl group;

R^(a4) and R^(a5) independently represent a hydrogen atom or a methyl group;

R^(a6) and R^(a7) independently represent a C₁ to C₈ alkyl group or a C₃ to C₁₀ alicyclic hydrocarbon group;

m1 represents an integer 0 to 14;

n1 represents an integer 0 to 10; and

n1′ represents an integer 0 to 3.

In the formula (a1-1) and the formula (a1-2), L^(a1) and L^(a2) are preferably *—O— or *—O—(CH₂)_(k1′)—CO—O—, here k1′ represents an integer of 1 to 4 and more preferably 1, and more preferably *—O.

R^(a4) and R^(a5) are preferably a methyl group.

Examples of the alkyl group of R^(a6) and R^(a7) include methyl, ethyl, propyl, butyl, pentyl, hexyl and octyl groups. Among these, the alkyl group of R^(a6) and R^(a7) is preferably a C₁ to C₆ alkyl group,

Examples of the alicyclic group of R^(a6) and R^(a7) include monocyclic hydrocarbon groups such as cyclopentyl, cyclohexyl, methylcyclohexyl, dimethylcyclohexyl, cycloheptyl, cyclooctyl groups; and polycyclic hydrocarbon groups such as decahydronaphtyl, adamantyl, norbornyl (i.e., bicyclo[2.2.1]hexyl), and methyl norbornyl groups as well as groups below. Among these, the alicyclic group of R^(a6) and R^(a7) is preferably a C₃ to C₈ alicyclic hydrocarbon group, and more preferably a C₃ to C₆ alicyclic hydrocarbon group.

m1 is preferably an integer of 0 to 3, and more preferably 0 or 1.

n1 is preferably an integer of 0 to 3, and more preferably 0 or 1.

n1′ is preferably 0 or 1, and more preferably 1.

Examples of the monomer (a1-1) include monomers described in JP 2010-204646A. Among these, the monomers are preferably monomers represented by the formula (a1-1-1) to the formula (a1-1-8), and more preferably monomers represented by the formula (a1-1-1) to the formula (a1-1-4) below.

Examples of the monomer (a1-2) include 1-ethylcyclopentane-1-yl (meth)acrylate, 1-ethylcyclohexane-1-yl (meth)acrylate, 1-ethylcycloheptane-1-yl (meth)acrylate, 1-methylcyclopentane-1-yl (meth)acrylate and 1-isopropylcyclopentane-1-yl (meth)acrylate. Among these, the monomers are preferably monomers represented by the formula (a1-2-1) to the formula (a1-2-6), and more preferably monomers represented by the formula (a1-2-3) and the formula (a1-2-4), and still more preferably monomer represented by the formula (a1-2-3) below.

When the resin (A2) contains the structural unit derived from the monomer (a1-1) and/or the structural unit derived from the monomer (a1-2), the total proportion thereof is generally 10 to 95 mol %, preferably 15 to 90 mol %, more preferably 20 to 85 mol %, with respect to the total structural units (100 mol %) of the resin (A2).

Examples of a monomer having an acid-labile group (2) and a carbon-carbon double bond include a monomer represented by the formula (a1-5). Such monomer may be hereinafter referred to as “monomer (a1-5)”. When the resin (A2) has the structural unit derived from the monomer (a1-5), a resist pattern tends to be obtained with less defects.

wherein R³¹ represents a hydrogen atom, a halogen atom or a C₁ to C₆ alkyl group that optionally has a halogen atom;

L¹, L² and L³ independently represent *—O—, *—S— or *—O—(CH₂)_(k1)—CO—O—, k1 represents an integer of 1 to 7, * represents a bond to the carbonyl group (—CO—);

s1 represents an integer of 0 to 4;

s1′ represents an integer of 0 to 4;

Z¹ represents a single bond or a C₁ to C₆ alkanediyl group, and one or more —CH₂— contained in the alkanediyl group may be replaced by —O— or —CO—.

In the formula (a1-5), R³¹ is preferably a hydrogen atom, a methyl group or trifluoromethyl group;

L¹ is preferably —O—;

L² and L³ are independently preferably *—O— or *—S—, and more preferably —O— for one and —S— for another;

s1 is preferably 1;

s1′ is preferably an integer of 0 to 2;

Z¹ is preferably a single bond or —CH₂—CO—O—.

Examples of the compound represented by the formula (a1-5) include compounds below.

When the resin (A2) contains the structural unit derived from the monomer represented by the formula (a1-5), the proportion thereof is generally 1 to 50 mol %, preferably 3 to 45 mol %, and more preferably 5 to 40 mol %, with respect to the total structural units (100 mol %) constituting the resin (A2).

<Acid Stable Monomer>

As the acid stable monomer, a monomer having a hydroxy group or a lactone ring is preferable. When a resin containing the structural unit derived from a monomer having hydroxy group (hereinafter such acid stable monomer may be referred to as “acid stable monomer (a2)”) or a acid stable monomer having a lactone ring (hereinafter such acid stable monomer may be referred to as “acid stable monomer (a3)”) is used, the adhesiveness of resist to a substrate and resolution of resist tend to be improved.

<Acid Stable Monomer (a2)>

The acid stable monomer (a2), which has the hydroxy group, is preferably selected depending on the kinds of an exposure light source at producing the resist pattern.

When KrF excimer laser lithography (248 nm), or high-energy irradiation such as electron beam or EUV light is used for the resist composition, using the acid stable monomer having a phenolic hydroxy group such as hydroxystyrene as the acid stable monomer (a2) is preferable.

When ArF excimer laser lithography (193 nm), i.e., short wavelength excimer laser lithography is used, using the acid stable monomer having a hydroxy adamantyl group represented by the formula (a2-1) as the acid stable monomer (a2) is preferable.

The acid stable monomer (a2) having the hydroxy group may be used as a single monomer or as a combination of two or more monomers.

Examples of the acid stable monomer having hydroxy adamantyl include the monomer represented by the formula (a2-1).

wherein L^(a3) represents —O— or *—O—(CH₂)_(k2)—CO—O—;

k2 represents an integer of 1 to 7;

-   -   * represents a bind to —CO—;

R^(a14) represents a hydrogen atom or a methyl group;

R^(a13) and R^(a16) independently represent a hydrogen atom, a methyl group or a hydroxy group;

o1 represents an integer of 0 to 10.

In the formula (a2-1), L^(a3) is preferably —O—, —O—(CH₂)_(f1)—CO—O—, here f1 represents an integer of 1 to 4, and more preferably —O—.

R^(a14) is preferably a methyl group.

R^(a15) is preferably a hydrogen atom.

R^(a16) is preferably a hydrogen atom or a hydroxy group.

o1 is preferably an integer of 0 to 3, and more preferably an integer of 0 or 1.

Examples of the acid stable monomer (a2-1) include monomers described in JP 2010-204646A. Among these, the monomers are preferably monomers represented by the formula (a2-1-1) to the formula (a2-1-6), more preferably monomers represented by the formula (a2-1-1) to the formula (a2-1-4), and still more preferably monomers represented by the formula (a2-1-1) and the formula (a2-1-3) below.

When the resin (A2) contains the acid stable structural unit derived from the monomer represented by the formula (a2-1), the proportion thereof is generally 3 to 40 mol %, preferably 5 to 35 mol %, more preferably 5 to 30 mol %, and still more preferably 5 to 20 mol %, with respect to the total structural units (100 mol %) constituting the resin (A2).

<Acid Stable Monomer (a3)>

The lactone ring included in the acid stable monomer (a3) may be a monocyclic compound such as β-propiolactone ring, γ-butyrolactone, δ-valerolactone, or a condensed ring with monocyclic lactone ring and other ring. Among these, γ-butyrolactone and condensed ring with γ-butyrolactone and other ring are preferable.

Examples of the acid stable monomer (a3) having the lactone ring include monomers represented by the formula (a3-1), the formula (a3-2) and the formula (a3-3). These monomers may be used as a single monomer or as a combination of two or more monomers.

wherein Lao to Lab independently represent —O— or *—O—(CH₂)_(k3)—CO—O—;

k3 represents an integer of 1 to 7, * represents a bind to —CO—;

R^(a18) to R^(a20) independently represent a hydrogen atom or a methyl group;

R^(a21) in each occurrence represents a C₁ to C₄ alkyl group;

p1 represents an integer of 0 to 5;

R^(a22) to R^(a23) in each occurrence independently represent a carboxyl group, cyano group, and a C₁ to C₄ alkyl group;

q1 and r1 independently represent an integer of 0 to 3.

In the formulae (a3-1) to (a3-3), Lao to Lab include the same group as described in L^(a3) above, and are independently preferably —O—, *—O—(CH₂)_(k3′)—CO—O—, here k3′ represents an integer of 1 to 4 (preferably 1), and more preferably —O—;

R^(a18) to R^(a21) are independently preferably a methyl group.

R^(a22) and R^(a23) are independently preferably a carboxyl group, cyano group or methyl group;

p1 to r1 are independently preferably an integer of 0 to 2, and more preferably an integer of 0 or 1.

Examples of the monomer (a3) include monomers described in JP 2010-204646A. Among these, the monomers are preferably monomers represented by the formula (a3-1-1) to the formula (a3-1-4), the formula (a3-2-1) to the formula (a3-2-4), the formula (a3-3-1) to the formula (a3-3-4), more preferably monomers represented by the formula (a3-1-1) to the formula (a3-1-2), the formula (a3-2-3) to the formula (a3-2-4), and still more preferably monomers represented by the formula (a3-1-1) and the formula (a3-2-3) below.

When the resin (A2) contains the structural units derived from the acid stable monomer (a3) having the lactone ring, the total proportion thereof is preferably 5 to 70 mol %, more preferably 10 to 65 mol %, still more preferably 15 to 60 mol %, with respect to the total structural units (100 mol %) constituting the resin (A2).

When the resin (A2) is the copolymer of the acid labile monomer (a1) and the acid stable monomer, the proportion of the structural unit derived from the acid labile monomer (a1) is preferably 10 to 80 mol %, and more preferably 20 to 60 mol %, with respect to the total structural units (100 mol %) constituting the resin (A2).

The proportion of the structural unit derived from the monomer having an adamantyl group (in particular, the monomer having the acid labile group (a1-1)) is preferably 15 mol % or more with respect to the structural units derived from the acid labile monomer (a1). As the mole ratio of the structural unit derived from the monomer having an adamantyl group increases within this range, the dry etching resistance of the resulting resist improves.

The resin (A2) preferably is a copolymer of the acid labile monomer (a1) and the acid stable monomer. In this copolymer, the acid labile monomer (a1) is preferably at least one of the acid labile monomer (a1-1) having an adamantyl group and the acid labile monomer (a1-2) having a cyclohexyl group, and more preferably is the acid labile monomer (a1-1).

The acid stable monomer is preferably the acid stable monomer (a2) having a hydroxy group and/or the acid stable monomer (a3) having a lactone ring. The acid stable monomer (a2) is preferably the monomer having the hydroxyadamantyl group (a2-1).

The acid stable monomer (a3) is preferably at least one of the monomer having the γ-butyrolactone ring (a3-1) and the monomer having the condensed ring of the γ-butyrolactone ring and the norbornene ring (a3-2).

The resin (A2) can be produced by a known polymerization method, for example, radical polymerization method, using at least one of the acid labile monomer (a1) and/or at least one of the acid stable monomer (a2) having a hydroxy group and/or at least one of the acid stable monomer (a3) having a lactone ring and/or at least one of a known compound.

The weight average molecular weight of the resin (A2) is preferably 2,500 or more (more preferably 3,000 or more, and still more preferably 4,000 or more), and 50,000 or less (more preferably 30,000 or less, and still more preferably 15,000 or less).

In the present resist composition, the weight ratio of the resins (A1)/(A2) (weight ratio) is preferably, for example, 0.01/10 to 5/10, more preferably 0.05/10 to 3/10, still more preferably 0.1/10 to 2/10, in particular, preferably 0.2/10 to 1/10.

<Resin Other than Resin (A1) and Resin (A2)>

The resist composition of the present invention may include a resin other than the resin (A1) and the resin (A2) described above. Such resin is a resin having a structural unit derived from the acid labile monomer, the acid stable monomer, as described above, and/or a known monomer in this field.

When the resist composition of the present invention include a resin other than the resin (A1) and the resin (A2), the proportion thereof is generally 0.1 to 50 weight %, preferably 0.5 to 30 weight %, and more preferably 1 to 20 weight %, with respect to the total structural units (100 weight %) of the resin (A) in the resist composition.

The proportion of the resin (A) can be adjusted with respect to the total solid proportion of the resist composition. For example, the resist composition of the present invention preferably contains 80 weight % or more and 99 weight % or less of the resin (A), with respect to the total solid proportion of the resist composition.

In the specification, the term “solid proportion of the resist composition” means the entire proportion of all ingredients other than the solvent (E). For example, if the proportion of the solvent (E) is 90 weight %, the solid proportion of the resist composition is 10 weight %.

The proportion of the resin (A) and the solid proportion of the resist composition can be measured with a known analytical method such as, for example, liquid chromatography and gas chromatography.

<Acid Generator (B)>

The acid generator (B) is classified into non-ionic-based or ionic-based acid generator. The present resist composition may be used either acid generators.

Examples of the non-ionic-based acid generator include organic halogenated compounds; sulfonate esters such as 2-nitrobenzyl ester, aromatic sulfonate, oxime sulfonate, N-sulfonyl oxyimide, sulfonyl oxyketone and diazo naphthoquinone 4-sulfonate; sulfones such as disulfone, ketosulfone and sulfone diazomethane.

Examples of the ionic acid generator includes onium salts containing onium cation (such as diazonium salts, phosphonium salts, sulfonium salts, iodonium salts).

Examples of anion of onium salts include sulfonate anion, sulfonylimide anion and sulfonylmethyde anion.

For the acid generator (B), compounds which generate an acid by radiation described in JP S63-26653-A, JP S55-164824-A, JP S62-69263-A, JP S63-146038-A, JP S63-163452-A, JP S62-153853-A, JP S63-146029-A, U.S. Pat. No. 3,779,778-B, U.S. Pat. No. 3,849,137-B, DE3,914,407-B and EP-126,712-A can be used.

Also, as the acid generator (B), compounds formed according to conventional methods can be used

The acid generator (B) is preferably a fluorine-containing acid generator represented by the formula (B1) as described below. In the acid generator (B1), electropositive Z⁺ hereinafter may be referred to as “an organic cation”, and electronegative one in which the organic cation has been removed from the compound may be referred to as “sulfonate anion”.

wherein Q¹ and Q² independently represent a fluorine atom or a C₁ to C₆ perfluoroalkyl group;

L^(b1) represents a single bond or an C₁ to C₁₇ divalent saturated hydrocarbon group, and one or more —CH₂— contained in the divalent saturated hydrocarbon group may be replaced by —O— or —CO—;

Y represents an optionally substituted C₁ to C₁₈ alkyl group or an optionally substituted C₃ to C₁₈ alicyclic hydrocarbon group, and one or more —CH₂— contained in the alkyl group and alicyclic hydrocarbon group may be replaced by —O—, —CO— or —SO₂—; and

Z⁺ represents an organic cation.

Examples of the perfluoroalkyl group of Q¹ and Q² include trifluoromethyl, perfluoroethyl, perfluoropropyl, perfluoro-isopropyl, perfluorobutyl, perfluoro-sec-butyl, perfluoro-tert-butyl, perfluoropentyl and perfluorohexyl groups.

Among these, Q¹ and Q² independently are preferably trifluoromethyl or fluorine atom, and more preferably a fluorine atom.

Examples of the a divalent saturated hydrocarbon group of L^(b1) include any of;

a chain alkanediyl group such as methylene, ethylene, propane-1,3-diyl, propane-1,2-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl, heptane-1,7-diyl, octane-1,8-diyl, nonane-1,9-diyl, decane-1,10-diyl, undecane-1,11-diyl, dodecane-1,12-diyl, tridecane-1,13-diyl, tetradecane-1,14-diyl, pentadecane-1,15-diyl, hexadecane-1,16-diyl, heptadecane-1,17-diyl groups, methane-1,1-diyl, ethane-1,1-diyl, propan-1,1-diyl and propan-2,2-diyl groups;

a branched chain alkanediyl group such as a group in which a chain alkanediyl group is bonded a side chain of a C₁ to C₄ alkyl group such as methyl, ethyl, propyl, isopropyl, butyl, sec-butyl and tert-butyl, for example, butan-1,3-diyl, 2-methylpropane-1,3-diyl, 2-methylpropane-1,2-diyl, pentane-1,4-diyl, 2-methylbutane-1,4-diyl groups;

a mono-alicyclic hydrocarbon group such as a cycloalkanediyl group (e.g., cyclobutan-1,3-diyl, cyclopentan-1,3-diyl, cyclohexane-1,2-diyl, 1-methylhexane-1,2-diyl, cyclohexane-1,4-diyl, cyclooctan-1,2-diyl, cyclooctan-1,5-diyl groups);

a poly-alicyclic hydrocarbon group such as norbornane-1,4-diyl, norbornane-2,5-diyl, adamantane-1,5-diyl and adamantane-2,6-diyl groups; and

a combination of two or more groups.

Examples of the saturated hydrocarbon group of L^(b1) in which one or more —CH₂— contained in the saturated hydrocarbon group is replaced by —O— or —CO— include groups represented by the formula (b1-1) to the formula (b1-6) below. In the formula (b1-1) to the formula (b1-6), the group is represented so as to correspond with two sides of the formula (B1), that is, the left side of the group bonds to C(Q¹)(Q²)- and the right side of the group bonds to —Y (examples of the formula (b1-1) to the formula (b1-6) are the same as above). * represents a bond.

wherein L^(b2) represents a single bond or a C₁ to C₁₅ divalent saturated hydrocarbon group;

L^(b3) represents a single bond or a C₁ to C₁₂ divalent saturated hydrocarbon group;

L^(b4) represents a C₁ to C₁₃ divalent saturated hydrocarbon group, the total number of the carbon atoms in L^(b3) and L^(b4) is at most 13;

L^(b5) represents a C₁ to C₁₅ divalent saturated hydrocarbon group;

L^(b6) and L^(b7) independently represent a C₁ to C₁₅ divalent saturated hydrocarbon group, the total number of the carbon atoms in L^(b6) and L^(b7) is at most 16;

L^(b8) represents a C₁ to C₁₄ divalent saturated hydrocarbon group; L^(b9) and L^(b10) independently represent a C₁ to C₁₁ divalent saturated hydrocarbon group, the total number of the carbon atoms in L^(b9) and L^(b10) is at most 12.

Among these, L^(b1) is preferably the groups represented by the formula (b1-1) to the formula (b1-4), more preferably the group represented by the formula (b1-1) or the formula (b1-2), and still more preferably the group represented by the formula (b1-1). In particular, the divalent group represented by the formula (b1-1) in which L^(b2) represents a single bond or —CH₂— is preferable.

Specific examples of the divalent group represented by the formula (b1-1) include groups below. In the formula below, * represent a bond.

Specific examples of the divalent group represented by the formula (b1-2) include groups below.

Specific examples of the divalent group represented by the formula (b1-3) include groups below.

Specific examples of the divalent group represented by the formula (b1-4) include a group below.

Specific examples of the divalent group represented by the formula (b1-5) include groups below.

Specific examples of the divalent group represented by the formula (b1-6) include groups below.

Examples of the alkyl group of Y include methyl, ethyl, 1-methylethyl, 1,1-dimethylethyl, 2,2-dimethylethyl, propyl, 1-methylpropyl, 2,2-dimethylpropyl, 1-ethylpropyl, butyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-propylbutyl, pentyl, 1-methylpentyl, hexyl, 1,4-dimethylhexyl, heptyl, 1-methylheptyl, octyl, methyloctyl, methylnonyl, 2-ethylhexyl, nonyl, decyl, undecyl and dodecyl groups.

The alkyl group of Y is preferably a C₁ to C₆ alkyl group.

Examples of the alicyclic hydrocarbon group of Y include groups represented by the formula (Y1) to the formula (Y11).

The alicyclic group of Y is preferably a C₃ to C₁₂ alicyclic hydrocarbon group.

Y may have a substituent.

Examples of the substituent of Y include a halogen atom, a hydroxy group, an oxo group, a C₁ to C₁₂ alkyl group, a hydroxy group-containing C₁ to C₁₂ alkyl group, a C₃ to C₁₆ alicyclic hydrocarbon group, a C₁ to C₁₂ alkoxy group, a C₆ to C₁₈ aromatic hydrocarbon group, a C₇ to C₂₁ aralkyl group, a C₂ to C₄ acyl group, a glycidyloxy group or a —(CH₂)_(j2)—O—CO—R^(b1) group, wherein R^(b1) represents a C₁ to C₁₆ alkyl group, a C₃ to C₁₆ alicyclic hydrocarbon group or a C₆ to C_(is) aromatic hydrocarbon group, j2 represents an integer of 0 to 4. The alkyl group, alicyclic hydrocarbon group, aromatic hydrocarbon group and the aralkyl group of the substituent may further have a substituent such as a C₁ to C₆ alkyl group, a halogen atom, a hydroxy group and an oxo group.

Examples of the hydroxy group-containing alkyl group include hydroxymethyl and hydroxyethyl groups

Examples of the aralkyl group include benzyl, phenethyl, phenylpropyl, naphthylmethyl and naphthylethyl groups.

Examples of alicyclic hydrocarbon group of Y in which one or more —CH₂— contained in the alicyclic hydrocarbon group is replaced by —O—, —CO— or —SO₂— include groups represented by the formula (Y12) to the formula (Y26).

Among these, the alicyclic hydrocarbon group is preferably any one of groups represented by the formula (Y1) to the formula (Y19), more preferably any one of groups represented by the formula (Y11), (Y14), (Y15) or (Y19), and still more preferably group represented by the formula (Y11) or (Y14).

Examples of Y include the groups below.

When Y represents an alkyl group and L^(b1) represents a C₁ to C₁₇ divalent alicyclic hydrocarbon group, the —CH₂— contained in the divalent alicyclic hydrocarbon group bonding Y is preferably replaced by an oxygen atom or carbonyl group. In this case, the —CH₂— contained in the alkyl group constituting Y is not replaced by an oxygen atom or carbonyl group.

Y is preferably an optionally substituted C₃ to C₁₈ alicyclic hydrocarbon group, more preferably an adamantyl group which is optionally substituted, for example, an oxo group and a hydroxy group, and still more preferably an adamantyl group, a hydroxyadamantyl group and an oxoadamantyl group.

The sulfonate anion is preferably a sulfonate anions represented by the formula (b1-1-1) to the formula (b1-1-9) below. In the formula (b1-1-1) to the formula (b1-1-9), Q¹, Q² and L^(b2) represents the same meaning as defined above. R^(b2) and R^(b3) independently represent a C₁ to C₄ alkyl group (preferably methyl group).

Specific examples of the sulfonate anion include sulfonate anions described in JP2010-204646A.

Examples of the cation of the acid generator (B) include an organic onium cation, for example, organic sulfonium cation, organic iodonium cation, organic ammonium cation, benzothiazolium cation and organic phosphonium cation. Among these, organic sulfonium cation and organic iodonium cation are preferable, and aryl sulfonium cation is more preferable.

Z⁺ of the formula (B1) is preferably represented by any of the formula (b2-1) to the formula (b2-4).

wherein R^(b4), R^(b5) and R^(b6) independently represent a C₁ to C₃₀ hydrocarbon group, the hydrocarbon group is preferably a C₁ to C₃₀ alkyl group, a C₅ to C₁₈ alicyclic hydrocarbon group or a C₆ to C₁₈ aromatic hydrocarbon group, the alkyl group may be substituted with a hydroxy group, a C₁ to C₁₂ alkoxy group or a C₆ to C₁₈ aromatic hydrocarbon group, the alicyclic hydrocarbon group may be substituted with a halogen atom, a C₂ to C₄ acyl group and a glycidyloxy group, the aromatic hydrocarbon group may be substituted with a halogen atom, a hydroxy group, a C₁ to C₁₈ alkyl group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₁ to C₁₂ alkoxy group;

R^(b7) and R^(b8) in each occurrence independently represent a hydroxy group, a C₁ to C₁₂ alkyl group or a C₁ to C₁₂ alkoxyl group;

m2 and n2 independently represent an integer of 0 to 5;

R^(b9) and R^(b10) independently represent a C₁ to C₁₈ alkyl group or a C₃ to C₁₈ alicyclic hydrocarbon group, or R^(b9) and R^(b10) may be bonded together with a sulfur atom bonded thereto to form a sulfur-containing 3- to 12-membered (preferably 3- to 7-membered) ring, and one or more —CH₂— contained in the ring may be replaced by —O—, —S— or —CO—;

R^(b11) represents a hydrogen atom, a C₁ to C₁₈ alkyl group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₆ to C₁₈ aromatic hydrocarbon group;

R^(b12) represents a C₁ to C₁₂ alkyl group, a C₃ to C₁₈ alicyclic hydrocarbon group and a C₆ to C₁₈ aromatic hydrocarbon group, the aromatic hydrocarbon group may be substituted with a C₁ to C₁₂ alkyl group, a C₁ to C₁₂ alkoxy group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₁ to C₁₂ alkyl carbonyloxy group;

R^(b11) and R^(b12) may be bonded together with —CH—CO— bonded thereto to form a 3- to 12-membered (preferably a 3- to 7-membered) ring, and one or more —CH₂— contained in the ring may be replaced by —O—, —S— or —CO—;

R^(b13), R^(b14), R^(b15), R^(b16), R^(b17) and R^(b18) in each occurrence independently represent a hydroxy group, a C₁ to C₁₂ alkyl group or a C₁ to C₁₂ alkoxy group;

L^(b11) represents —S— or —O—;

o2, p2, s2 and t2 independently represent an integer of 0 to 5;

q2 or r2 independently represent an integer of 0 to 4;

u2 represents an integer of 0 or 1.

Examples of the alkyl group include methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, octyl and 2-ethylhexyl groups. In particular, the alkyl group of R^(b9) to R^(b11) is preferably a C₁ to C₁₂ alkyl group.

Examples of the alicyclic hydrocarbon group include a monocyclic hydrocarbon groups such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclodecyl, 2-alkyladamantane-2-yl, 1-(adamatane-1-yl)-1-alkyl and isobornyl groups. In particular, the alicyclic hydrocarbon group of R^(b9) to R^(b11) is preferably a C₃ to C₁₈ alicyclic hydrocarbon group and more preferably a C₄ to C₁₂ alicyclic hydrocarbon group.

Examples of the aromatic hydrocarbon group include phenyl, naphthyl, 4-methylphenyl, 4-ethylphenyl, 4-t-butylphenyl, 4-cyclohexylphenyl, 4-methoxyphenyl and biphenyl groups.

Examples of the aromatic group substituted with an alkyl group typically represent an aralkyl group such as benzyl and phenethyl groups.

Examples of the alkoxy group include methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy, heptyloxy, octyloxy, decyloxy and dodecyloxy groups.

Examples of the halogen atom include chlorine, bromine and iodine atoms.

Examples of the acyl group include acetyl, propionyl and butyryl groups.

Examples of the alkyl carbonyloxy group of the R^(b12) include methyl carbonyloxy, ethyl carbonyloxy, n-propyl carbonyloxy, isopropyl carbonyloxy, n-butyl carbonyloxy, sec-butyl carbonyloxy, tert-butyl carbonyloxy, pentyl carbonyloxy, hexyl carbonyloxy, octylcarbonyloxy and 2-ethylhexylcarbonyloxy groups.

Examples of the ring having —CH—CO— and formed by R^(b9) and R^(b10) bonded together include thiolane-1-ium ring (tetrahydrothiophenium ring), thian-1-ium ring and 1,4-oxathian-4-ium ring.

Examples of the ring having a sulfur atom and formed by R^(b11) and R^(b12) bonded together include oxocycloheptane ring, oxocyclohexane ring, oxonorbornane ring and oxoadamantane ring.

Among the cations represented by the formula (b2-1) to the formula (b2-4), the cation represented by the formula (b2-1-1) is preferable, and triphenyl sulfonium cation (v2=w2=x2=0 in the formula (b2-1-1)), diphenyltolyl sulfonium cation (v2=w2=0, x2=1, and R^(b21) is a methyl group in the formula (b2-1-1)) and tritolyl sulfonium cation (v2=w2=x2=1, R^(b19), R^(b20) and R^(b21) are a methyl group in the formula (b2-1-1)) are more preferable.

wherein R^(b19), R^(b20) and R^(b21) in each occurrence independently represent a halogen atom, a hydroxy group, a C₁ to C₁₂ alkyl group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₁ to C₁₂ alkoxy group, and the alkyl group, the alicyclic hydrocarbon group and the alkoxy group may be substituted with a halogen group, a hydroxy group, a C₁ to C₁₂ alkoxy group, a C₆ to C₁₈ aromatic hydrocarbon group, a C₂ to C₄ acyl group or a glycidyloxy group;

v2 to x2 independently represent an integer of 0 to 5.

In the formula (b2-1-1), R^(b19) to R^(b21) independently preferably represent a halogen atom (and more preferably fluorine atom), a hydroxy group, a C₁ to C₁₂ alkyl group or a C₁ to C₁₂ alkoxy group; and

v2 to x2 independently represent preferably 0 or 1.

Specific examples of the organic cations represented by the formula (b2-1) to the formula (b2-4) include, for example, compounds described in JP2010-204646A.

Preferred acid generators (B1) are represented by the formula (B1-1) to the formula (B1-17). Among these, the formulae (B1-1), (B1-2), (B1-6), (B1-11), (B1-12), (B1-13) and (B1-14) which contain triphenyl sulfonium cation, and the formulae (B1-3) and (B1-7) which contain tritolyl sulfonium cation are preferable.

The proportion of the acid generator (B) is preferably not less than 1 parts by weight (and more preferably not less than 3 parts by weight), and not more than 30 parts by weight (and more preferably not more than 25 parts by weight), with respect to 100 parts by weight of the resin (A2).

In the resist composition of the present invention, the acid generator may be used as a single salt or as a combination of two or more salts.

<Salt (IA)>

The salt (IA) is represented by the formula (IA).

wherein R^(1A) and R^(2A) independently represent a hydrogen atom, a C₁ to C₁₂ aliphatic hydrocarbon group, a C₃ to C₂₀ alicyclic hydrocarbon group, a C₆ to C₂₀ aromatic hydrocarbon group or a C₇ to C₂₁ aralkyl group, one or more hydrogen atom contained in the aliphatic hydrocarbon, the alicyclic hydrocarbon group, the aromatic hydrocarbon group and the aralkyl group may be replaced by a hydroxy group, a cyano group, a fluorine atom, a trifluoromethyl group or a nitro group, and one or more —CH₂— contained in the aliphatic hydrocarbon group may be replaced by —O— or —CO—, or R^(1A) and R^(2A) may be bonded together with a nitrogen atom bonded thereto to form a C₄ to C₂₀ ring.

Examples of the aliphatic hydrocarbon group include methyl (IR-1), ethyl (IR-2), n-propyl (IR-3), iso-propyl (IR-4) n-butyl (IR-5), sec-butyl (IR-6), tert-butyl (IR-7), n-pentyl (IR-8), n-hexyl (IR-9), heptyl (IR-10), octyl (IR-11), 2-ethylhexyl (IR-12), nonyl (IR-13), decyl (IR-14), undecyl (IR-15) and dodecyl (IR-16) groups.

The alicyclic hydrocarbon group may be either monocyclic or polycyclic hydrocarbon group. Examples of the alicyclic hydrocarbon group include cyclopropyl (IR-21), cyclobutyl (IR-22), cyclopentyl (IR-23), cyclohexyl (IR-24), cycloheptyl (IR-25), cyclooctyl (IR-26), cyclononyl (IR-27), cyclodecyl (IR-28), 1-norbornyl (IR-29), 1-adamantyl (IR-30), 2-adamantyl (IR-31), 2-isobonyl (IR-32), 2-norbornyl (IR-33) and groups described below.

Examples of the aromatic hydrocarbon group include phenyl (IR-51), 1-naphthyl (IR-52), 1-anthryl (IR-53), p-methylphenyl (IR-54), p-tert-butylphenyl (IR-55), p-adamantylphenyl (IR-56), 2-naphthyl (IR-57), 2-anthryl (IR-58) and 9-anthryl (IR-59) groups.

Examples of the aliphatic hydrocarbon group which is substituted with hydroxy group include groups described below.

Examples of the aliphatic hydrocarbon group which is substituted with cyano group include groups described below.

Examples of the aliphatic hydrocarbon group which is substituted with a fluorine atom include groups described below.

Examples of the aliphatic hydrocarbon group which is substituted with a nitro group include groups described below.

Examples of the alicyclic hydrocarbon group which is substituted with a hydroxy group include groups described below.

Examples of the alicyclic hydrocarbon group which is substituted with cyano group include groups described below.

Examples of the alicyclic hydrocarbon group which is substituted with fluorine atom or fluoromethyl group include groups described below.

Examples of the alicyclic hydrocarbon group which is substituted with a nitro group include groups described below.

Examples of the aromatic hydrocarbon group which is substituted with a hydroxy group include groups described below.

Examples of the aromatic hydrocarbon group which is substituted with a cyano group include groups described below.

Examples of the aromatic hydrocarbon group which is substituted with a fluorine atom or fluoromethyl group include groups described below.

Examples of the aromatic hydrocarbon group which is substituted with a nitro group include groups described below.

Examples of the aralkyl hydrocarbon group which is substituted with a hydroxy group include groups described below.

Examples of the aralkyl hydrocarbon group which is substituted with a cyano group include groups described below.

Examples of the aralkyl hydrocarbon group which is substituted with a fluorine atom or fluorimethyl group include groups described below.

Examples of the aralkyl hydrocarbon group which is substituted with a nitro group include groups described below.

Examples of one or more —CH₂— contained in the aliphatic hydrocarbon group replaced by —O— include groups described below.

Examples of one or more —CH₂— contained in the aliphatic hydrocarbon group replaced by —CO— include groups described below.

Examples of two —CH₂— contained in the aliphatic hydrocarbon group replaced by —O— and —CO— include groups described below,

When R^(1A) and R^(2A) are bonded together with a nitrogen atom bonded thereto to form a ring, examples —NR^(1A)R^(2A) include groups described below. * represents a bond to SO₃—.

In the formula (IA), an anion in which one of R^(1A) and R^(2A) is an aliphatic hydrocarbon group or an aromatic hydrocarbon group, or an anion represented by the formula (IE) below is preferable.

wherein ring W¹ represents an optionally substituted heterocyclic ring.

Examples of the optionally substituted heterocyclic ring include groups represented by the formula (IR-301) to the formula (IR-329) described above. Among these, a group in which one of R^(1A) and R^(2A) is cyclohexyl group or adamantyl group, a group represented by the formula (IR-316), or a group represented by the formula (IR-326) is preferable.

The salt having an anion represented by the formula (IA) generally contains a cation.

Examples of the cation include an onium cation (such as diazonium cation, organic phosphonium cation, organic sulfonium cation, organic iodonium cation), among these, organic sulfonium cation and organic iodonium cation are preferable.

Examples of the cation include cations represented by the formulae (b2-1) to (b2-4) and the formula (b2-1-1), among these, the cations represented by the formula (IB), the formula (IC) and the formula (ID) which correspond to the cations represented by the formula (b2-3), the formula (b2-4) and the formula (b2-1-1) are preferable, and the cations represented by the formula (IB) is more preferable.

wherein R³, R⁴ and R⁵ in each occurrence independently represent a hydroxy group, a halogen atom, a C₁ to C₁₂ alkyl group, a C₁ to C₁₂ alkoxy group or a C₃ to C₁₈ alicyclic hydrocarbon group, and the alkyl group, the alkoxy group and the alicyclic hydrocarbon group may be substituted with a halogen group, a hydroxy group, a C₁ to C₁₂ alkoxy group, a C₆ to C₁₈ aromatic hydrocarbon group, a C₂ to C₄ acyl group or a glycidyloxy group;

mx to m/z independently represent an integer of 0 to 5.

Specific examples of the cation represented by the formula (IB) include cations below.

R⁶ and R⁷ independently represent a C₁ to C₃₆ aliphatic hydrocarbon group or a C₃ to C₃₆ alicyclic hydrocarbon group, or R⁶ and R⁷ may be bonded together with a sulfur atom bonded thereto to form a sulfur-containing 3- to 12-membered ring, and one or more —CH₂-contained in the ring may be replaced by —O—, —S— or —CO—;

R⁸ represents a hydrogen atom, a C₁ to C₃₆ aliphatic hydrocarbon group, a C₃ to C₃₆ alicyclic hydrocarbon group or a C₆ to C₁₈ aromatic hydrocarbon group;

R⁹ represents a C₁ to C₁₂ aliphatic hydrocarbon group, a C₃ to C₁₈ alicyclic hydrocarbon group and a C₆ to C₁₈ aromatic hydrocarbon group, the aromatic hydrocarbon group may be substituted with a C₁ to C₁₂ aliphatic hydrocarbon group, a C₁ to C₁₂ alkoxy group, a C₃ to C₁₈ alicyclic hydrocarbon group or a C₁ to C₁₂ alkyl carbonyloxy group;

R⁸ and R⁹ may be bonded together with —CH—CO— bonded thereto to form a 3- to 12-membered ring, and one or more —CH₂— contained in the ring may be replaced by —O—, —S— or —CO—.

In particular, the aliphatic hydrocarbon group of R⁶ to R⁸ is preferably a C₁ to C₁₂ aliphatic hydrocarbon group, the alicyclic hydrocarbon group of R⁶ to R⁸ is preferably a C₃ to C₃₆ alicyclic hydrocarbon group, and more preferably a C₄ to C₁₂ alicyclic hydrocarbon group.

Specific examples of the cation represented by the formula (IC) include cations below.

R^(3d) and R^(4d) in each occurrence independently represent a C₁ to C₃₀ aliphatic hydrocarbon group, a C₃ to C₃₆ alicyclic hydrocarbon group or a C₆ to C₁₈ aromatic hydrocarbon group, one or more hydrogen atom contained in the aliphatic hydrocarbon group may be substituted with a hydroxy group, a C₁ to C₁₂ alkoxy group or a C₆ to C₁₈ aromatic hydrocarbon group, one or more hydrogen atom contained in the alicyclic hydrocarbon group may be substituted with a halogen atom, a C₂ to C₄ acyl group or a glycidyloxy group and one or more hydrogen atom contained in the aromatic hydrocarbon group may be substituted with a halogen atom, a hydroxy group, a C₁ to C₃₆ aliphatic hydrocarbon group, a C₃ to C₃₆ alicyclic hydrocarbon group or a C₆ to C₁₂, alkoxy group;

md and md′ independently represent an integer of 0 to 5.

Specific examples of the cation represented by the formula (ID) include cations below.

Examples of the sulfonium salts having an anion represented by the formula (IA) include sulfonium salts described in the Tables below. In the Table, “IR-1”, for example, means the group represented by the formula (IR-1) described above, and “I-1” hereinafter may be expressed “salt represented by the formula (I-1)”,

TABLE 1 Salt R^(1A) R^(2A) Cation I-1 H IR-1 IB-1 I-2 H IR-2 IB-1 I-3 H IR-3 IB-1 I-4 H IR-4 IB-1 I-5 H IR-5 IB-1 I-6 H IR-6 IB-1 I-7 H IR-7 IB-1 I-8 H IR-8 IB-1 I-9 H IR-9 IB-1 I-10 H IR-10 IB-1 I-11 H IR-11 IB-1 I-12 H IR-12 IB-1 I-13 H IR-13 IB-1 I-14 H IR-14 IB-1 I-15 H IR-15 IB-1 I-16 H IR-16 IB-1

TABLE 2 Salt R^(1A) R^(2A) Cation I-17 H IR-21 IB-1 I-18 H IR-22 IB-1 I-19 H IR-23 IB-1 I-20 H IR-24 IB-1 I-21 H IR-25 IB-1 I-22 H IR-26 IB-1 I-23 H IR-27 IB-1 I-24 H IR-28 IB-1 I-25 H IR-29 IB-1 I-26 H IR-30 IB-1 I-27 H IR-31 IB-1 I-28 H IR-32 IB-1 I-29 H IR-33 IB-1 I-30 H IR-34 IB-1 I-31 H IR-35 IB-1 I-32 H IR-36 IB-1

TABLE 3 Salt R^(1A) R^(2A) Cation I-33 H IR-37 IB-1 I-34 H IR-38 IB-1 I-35 H IR-51 IB-1 I-36 H IR-52 IB-1 I-37 H IR-53 IB-1 I-38 H IR-54 IB-1 I-39 H IR-55 IB-1 I-40 H IR-56 IB-1 I-41 H IR-61 IB-1

TABLE 4 Salt R^(1A) R^(2A) Cation I-42 H IR-91 IB-1 I-43 H IR-92 IB-1 I-44 H IR-93 IB-1 I-45 H IR-94 IB-1 I-46 H IR-95 IB-1 I-47 H IR-96 IB-1 I-48 H IR-101 IB-1 I-49 H IR-102 IB-1 I-50 H IR-103 IB-1 I-51 H IR-104 IB-1 I-52 H IR-105 IB-1 I-53 H IR-106 IB-1 I-54 H IR-111 IB-1 I-55 H IR-112 IB-1 I-56 H IR-113 IB-1 I-57 H IR-114 IB-1 I-58 H IR-115 IB-1 I-59 H IR-116 IB-1 I-60 H IR-117 IB-1 I-61 H IR-118 IB-1 I-61-1 H IR-119 IB-1 I-62 H IR-121 IB-1 I-63 H IR-122 IB-1 I-64 H IR-123 IB-1 I-65 H IR-124 IB-1 I-66 H IR-125 IB-1 I-67 H IR-126 IB-1

TABLE 5 Salt R^(1A) R^(2A) Cation I-68 H IR-131 IB-1 I-69 H IR-132 IB-1 I-70 H IR-133 IB-1 I-71 H IR-134 IB-1 I-72 H IR-135 IB-1 I-73 H IR-141 IB-1 I-74 H IR-142 IB-1 I-75 H IR-143 IB-1 I-76 H IR-144 IB-1 I-77 H IR-145 IB-1 I-78 H IR-151 IB-1 I-79 H IR-152 IB-1 I-80 H IR-153 IB-1 I-81 H IR-154 IB-1 I-82 H IR-155 IB-1 I-82-1 H IR-156 IB-1 I-82-2 H IR-157 IB-1 I-82-3 H IR-158 IB-1 I-82-4 H IR-159 IB-1 I-83 H IR-161 IB-1 I-84 H IR-162 IB-1 I-85 H IR-163 IB-1 I-86 H IR-164 IB-1 I-87 H IR-165 IB-1

TABLE 6 Salt R^(1A) R^(2A) Cation I-88 H IR-171 IB-1 I-89 H IR-172 IB-1 I-90 H IR-173 IB-1 I-91 H IR-174 IB-1 I-92 H IR-181 IB-1 I-93 H IR-182 IB-1 I-94 H IR-183 IB-1 I-95 H IR-184 IB-1 I-96 H IR-191 IB-1 I-97 H IR-192 IB-1 I-98 H IR-193 IB-1 I-99 H IR-194 IB-1 I-100 H IR-195 IB-1 I-101 H IR-196 IB-1 I-102 H IR-197 IB-1 I-103 H IR-198 IB-1 I-104 H IR-199 IB-1 I-105 H IR-200 IB-1 I-106 H IR-211 IB-1 I-107 H IR-212 IB-1 I-108 H IR-213 IB-1 I-109 H IR-214 IB-1

TABLE 7 Salt R^(1A) R^(2A) Cation I-110 H IR-221 IB-1 I-111 H IR-231 IB-1 I-112 H IR-241 IB-1 I-112-1 H IR-245 IB-1 I-113 H IR-251 IB-1

TABLE 8 Salt R^(1A) R^(2A) Cation I-114 H IR-261 IB-1 I-115 H IR-262 IB-1 I-116 H IR-263 IB-1 I-117 H IR-264 IB-1 I-118 H IR-265 IB-1 I-119 H IR-266 IB-1 I-120 H IR-271 IB-1 I-121 H IR-272 IB-1 I-122 H IR-273 IB-1 I-123 H IR-274 IB-1 I-124 H IR-275 IB-1 I-125 H IR-276 IB-1 I-126 H IR-281 IB-1 I-127 H IR-282 IB-1 I-128 H IR-283 IB-1 I-129 H IR-284 IB-1 I-130 H IR-285 IB-1 I-131 H IR-286 IB-1

TABLE 9 Salt R^(1A) R^(2A) Cation I-132 IR-1 IR-1 IB-1 I-133 IR-2 IR-2 IB-1 I-134 IR-3 IR-3 IB-1 I-135 IR-4 IR-4 IB-1 I-136 IR-5 IR-5 IB-1 I-137 IR-6 IR-6 IB-1 I-138 IR-7 IR-7 IB-1 I-139 IR-8 IR-8 IB-1 I-140 IR-9 IR-9 IB-1 I-141 IR-10 IR-10 IB-1 I-142 IR-11 IR-11 IB-1 I-143 IR-12 IR-12 IB-1 I-144 IR-13 IR-13 IB-1 I-145 IR-14 IR-14 IB-1 I-146 IR-15 IR-15 IB-1 I-147 IR-16 IR-16 IB-1 I-148 IR-21 IR-21 IB-1 I-149 IR-22 IR-22 IB-1 I-150 IR-23 IR-23 IB-1 I-151 IR-24 IR-24 IB-1 I-152 IR-25 IR-25 IB-1 I-153 IR-26 IR-26 IB-1 I-154 IR-27 IR-27 IB-1 I-155 IR-28 IR-28 IB-1 I-156 IR-29 IR-29 IB-1 I-157 IR-30 IR-30 IB-1 I-158 IR-31 IR-31 IB-1 I-159 IR-32 IR-32 IB-1 I-160 IR-33 IR-33 IB-1 I-161 IR-34 IR-34 IB-1 I-162 IR-35 IR-35 IB-1 I-163 IR-36 IR-36 IB-1 I-164 IR-37 IR-37 IB-1 I-165 IR-38 IR-38 IB-1 I-166 H IR-287 IB-1 I-167 H IR-288 IB-1 I-168 H IR-289 IB-1 I-169 H IR-290 IB-1 I-170 IR-271 IR-23 IB-1 I-171 IR-271 IR-24 IB-1 I-172 IR-271 IR-30 IB-1

TABLE 10 Ring formed with Salt R^(1A), R^(2A) and N Cation I-201 IR-301 IB-1 I-202 IR-302 IB-1 I-203 IR-303 IB-1 I-204 IR-304 IB-1 I-205 IR-305 IB-1 I-206 IR-306 IB-1 I-207 IR-307 IB-1 I-208 IR-308 IB-1 I-209 IR-309 IB-1 I-210 IR-310 IB-1 I-211 IR-311 IB-1 I-212 IR-312 IB-1 I-213 IR-313 IB-1 I-214 IR-314 IB-1 I-215 IR-315 IB-1 I-216 IR-316 IB-1 I-217 IR-317 IB-1 I-218 IR-318 IB-1 I-219 IR-319 IB-1 I-220 IR-320 IB-1 I-221 IR-321 IB-1 I-222 IR-322 IB-1 I-223 IR-323 IB-1 I-224 IR-324 IB-1 I-225 IR-325 IB-1 I-226 IR-326 IB-1 I-227 IR-327 IB-1 I-228 IR-328 IB-1 I-229 IR-329 IB-1

TABLE 11 Salt R^(1A) R^(2A) Cation I-301 H IR-6 IB-10 I-302 H IR-6 IB-12 I-303 H IR-6 IB-21 I-304 H IR-6 IC-49 I-305 H IR-23 IB-10 I-306 H IR-23 IB-12 I-307 H IR-23 IB-21 I-308 H IR-23 IC-49 I-309 H IR-24 IB-10 I-310 H IR-24 IB-12 I-311 H IR-24 IB-21 I-312 H IR-24 IC-49 I-313 H IR-30 IB-10 I-314 H IR-30 IB-12 I-315 H IR-30 IB-21 I-316 H IR-30 IC-49 I-317 H IR-33 IB-10 I-318 H IR-33 IB-12 I-319 H IR-33 IB-21 I-320 H IR-33 IC-49 I-321 H IR-35 IB-10 I-322 H IR-35 IB-12 I-323 H IR-35 IB-21 I-324 H IR-35 IC-49

TABLE 12 Salt R^(1A) R^(2A) Cation I-325 H IR-113 IB-10 I-326 H IR-113 IB-12 I-327 H IR-113 IB-21 I-328 H IR-113 IC-49 I-329 H IR-131 IB-10 I-330 H IR-131 IB-12 I-331 H IR-131 IB-21 I-332 H IR-131 IC-49 I-333 H IR-151 IB-10 I-334 H IR-151 IB-12 I-335 H IR-151 IB-21 I-336 H IR-151 IC-49 I-337 H IR-172 IB-10 I-338 H IR-172 IB-12 I-339 H IR-172 IB-21 I-340 H IR-172 IC-49 I-341 H IR-194 IB-10 I-342 H IR-194 IB-12 I-343 H IR-194 IB-21 I-344 H IR-194 IC-49 I-345 IR-23 IR-23 IB-10 I-346 IR-23 IR-23 IB-12 I-347 IR-23 IR-23 IB-21 I-348 IR-23 IR-23 IC-49 I-349 IR-24 IR-24 IB-10 I-350 IR-24 IR-24 IB-12 I-351 IR-24 IR-24 IB-21 I-352 IR-24 IR-24 IC-49 I-353 H IR-287 IB-6 I-354 H IR-287 IB-10 I-355 H IR-287 IC-49 I-356 H IR-288 IB-6 I-357 H IR-288 IB-10 I-358 H IR-288 IC-49 I-359 H IR-289 IB-6 I-360 H IR-289 IB-10 I-361 H IR-289 IC-49 I-362 H IR-290 IB-6 I-363 H IR-290 IB-10 I-364 H IR-290 IC-49 I-365 H IR-193 IB-6 I-366 H IR-193 IB-10 I-367 H IR-193 IC-49 I-368 IR-271 IR-23 IB-10 I-369 IR-271 IR-24 IB-10 I-370 IR-271 IR-30 IB-10

TABLE 13 Ring formed with Salt R^(1A), R^(2A) and N Cation I-401 IR-306 IB-10 I-402 IR-306 IB-12 I-403 IR-306 IB-21 I-404 IR-306 IC-49 I-405 IR-314 IB-10 I-406 IR-314 IB-12 I-407 IR-314 IB-21 I-408 IR-314 IC-49 I-409 IR-316 IB-10 I-410 IR-316 IB-12 I-411 IR-316 IB-21 I-412 IR-316 IC-49 I-413 IR-305 IB-6 I-414 IR-305 IB-10 I-415 IR-305 IC-49 I-416 IR-326 IB-6 I-417 IR-326 IB-10 I-418 IR-326 IC-49 I-419 IR-327 IB-6 I-420 IR-327 IB-10 I-421 IR-327 IC-49 I-422 IR-328 IB-6 I-423 IR-328 IB-10 I-424 IR-328 IC-49 I-425 IR-329 IB-6 I-426 IR-329 IB-10 I-427 IR-329 IC-49

TABLE 14 Salt R^(1A) R^(2A) Cation I′-1 H IR-30 ID-11 I′-2 IR-1 IR-30 ID-11 I′-3 IR-2 IR-30 ID-11 I′-4 IR-3 IR-30 ID-11 I′-5 IR-4 IR-30 ID-11 I′-6 IR-5 IR-30 ID-11 I′-7 IR-6 IR-30 ID-11 I′-8 IR-7 IR-30 ID-11 I′-9 IR-8 IR-30 ID-11 I′-10 IR-9 IR-30 ID-11 I′-11 IR-10 IR-30 ID-11 I′-12 IR-11 IR-30 ID-11 I′-13 IR-12 IR-30 ID-11 I′-14 IR-13 IR-30 ID-11 I′-15 IR-14 IR-30 ID-11 I′-16 IR-15 IR-30 ID-11

TABLE 15 Salt R^(1A) R^(2A) Cation I′-17 IR-21 IR-30 ID-11 I′-18 IR-22 IR-30 ID-11 I′-19 IR-23 IR-30 ID-11 I′-20 IR-24 IR-30 ID-11 I′-21 IR-25 IR-30 ID-11 I′-22 IR-26 IR-30 ID-11 I′-23 IR-27 IR-30 ID-11 I′-24 IR-28 IR-30 ID-11 I′-25 IR-29 IR-30 ID-11 I′-26 IR-30 IR-30 ID-11 I′-27 IR-31 IR-30 ID-11 I′-28 IR-32 IR-30 ID-11 I′-29 IR-33 IR-30 ID-11 I′-30 IR-34 IR-30 ID-11 I′-31 IR-35 IR-30 ID-11 I′-32 IR-36 IR-30 ID-11

TABLE 16 Salt R^(1A) R^(2A) Cation I′-33 IR-37 IR-30 ID-11 I′-34 IR-38 IR-30 ID-11 I′-35 IR-51 IR-30 ID-11 I′-36 IR-52 IR-30 ID-11 I′-37 IR-53 IR-30 ID-11 I′-38 IR-54 IR-30 ID-11 I′-39 IR-55 IR-30 ID-11 I′-40 IR-56 IR-30 ID-11 I′-41 IR-61 IR-30 ID-11

TABLE 17 Salt R^(1A) R^(2A) Cation I′-42 IR-91 IR-30 ID-11 I′-43 IR-92 IR-30 ID-11 I′-44 IR-93 IR-30 ID-11 I′-45 IR-94 IR-30 ID-11 I′-46 IR-95 IR-30 ID-11 I′-47 IR-96 IR-30 ID-11 I′-48 IR-101 IR-30 ID-11 I′-49 IR-102 IR-30 ID-11 I′-50 IR-103 IR-30 ID-11 I′-51 IR-104 IR-30 ID-11 I′-52 IR-105 IR-30 ID-11 I′-53 IR-106 IR-30 ID-11 I′-54 IR-111 IR-30 ID-11 I′-55 IR-112 IR-30 ID-11 I′-56 IR-113 IR-30 ID-11 I′-57 IR-114 IR-30 ID-11 I′-58 IR-115 IR-30 ID-11 I′-59 IR-116 IR-30 ID-11 I′-60 IR-117 IR-30 ID-11 I′-61 IR-118 IR-30 ID-11 I′-61-1 IR-119 IR-30 ID-11 I′-62 IR-121 IR-30 ID-11 I′-63 IR-122 IR-30 ID-11 I′-64 IR-123 IR-30 ID-11 I′-65 IR-124 IR-30 ID-11 I′-66 IR-125 IR-30 ID-11 I′-67 IR-126 IR-30 ID-11

TABLE 18 Salt R^(1A) R^(2A) Cation I′-68 IR-131 IR-30 ID-11 I′-69 IR-132 IR-30 ID-11 I′-70 IR-133 IR-30 ID-11 I′-71 IR-134 IR-30 ID-11 I′-72 IR-135 IR-30 ID-11 I′-73 IR-141 IR-30 ID-11 I′-74 IR-142 IR-30 ID-11 I′-75 IR-143 IR-30 ID-11 I′-76 IR-144 IR-30 ID-11 I′-77 IR-145 IR-30 ID-11 I′-78 IR-151 IR-30 ID-11 I′-79 IR-152 IR-30 ID-11 I′-80 IR-153 IR-30 ID-11 I′-81 IR-154 IR-30 ID-11 I′-82 IR-155 IR-30 ID-11 I′-82-1 IR-156 IR-30 ID-11 I′-82-2 IR-157 IR-30 ID-11 I′-82-3 IR-158 IR-30 ID-11 I′-82-4 IR-159 IR-30 ID-11 I′-83 IR-161 IR-30 ID-11 I′-84 IR-162 IR-30 ID-11 I′-85 IR-163 IR-30 ID-11 I′-86 IR-164 IR-30 ID-11 I′-87 IR-165 IR-30 ID-11

TABLE 19 Salt R^(1A) R^(2A) Cation I′-88 IR-171 IR-30 ID-11 I′-89 IR-172 IR-30 ID-11 I′-90 IR-173 IR-30 ID-11 I′-91 IR-174 IR-30 ID-11 I′-92 IR-181 IR-30 ID-11 I′-93 IR-182 IR-30 ID-11 I′-94 IR-183 IR-30 ID-11 I′-95 IR-184 IR-30 ID-11 I′-96 IR-191 IR-30 ID-11 I′-97 IR-192 IR-30 ID-11 I′-98 IR-193 IR-30 ID-11 I′-99 IR-194 IR-30 ID-11 I′-100 IR-195 IR-30 ID-11 I′-101 IR-196 IR-30 ID-11 I′-102 IR-197 IR-30 ID-11 I′-103 IR-198 IR-30 ID-11 I′-104 IR-199 IR-30 ID-11 I′-105 IR-200 IR-30 ID-11 I′-106 IR-211 IR-30 ID-11 I′-107 IR-212 IR-30 ID-11 I′-108 IR-213 IR-30 ID-11 I′-109 IR-214 IR-30 ID-11

TABLE 20 Salt R^(1A) R^(2A) Cation I′-110 IR-221 IR-30 ID-11 I′-111 IR-231 IR-30 ID-11 I′-112 IR-241 IR-30 ID-11 I′-112-1 IR-245 IR-30 ID-11 I′-113 IR-251 IR-30 ID-11

TABLE 21 Salt R^(1A) R^(2A) Cation I′-114 IR-261 IR-30 ID-11 I′-115 IR-262 IR-30 ID-11 I′-116 IR-263 IR-30 ID-11 I′-117 IR-264 IR-30 ID-11 I′-118 IR-265 IR-30 ID-11 I′-119 IR-266 IR-30 ID-11 I′-120 IR-271 IR-30 ID-11 I′-121 IR-272 IR-30 ID-11 I′-122 IR-273 IR-30 ID-11 I′-123 IR-274 IR-30 ID-11 I′-124 IR-275 IR-30 ID-11 I′-125 IR-276 IR-30 ID-11 I′-126 IR-281 IR-30 ID-11 I′-127 IR-282 IR-30 ID-11 I′-128 IR-283 IR-30 ID-11 I′-129 IR-284 IR-30 ID-11 I′-130 IR-285 IR-30 ID-11 I′-131 IR-286 IR-30 ID-11 I′-132 IR-287 IR-30 ID-11 I′-133 IR-288 IR-30 ID-11 I′-134 IR-289 IR-30 ID-11 I′-135 IR-290 IR-30 ID-11

TABLE 22 Salt R^(1A) R^(2A) Cation I′-136 IR-10 IR-10 ID-11 I′-137 IR-11 IR-11 ID-11 I′-138 IR-12 IR-12 ID-11 I′-139 IR-13 IR-13 ID-11 I′-140 IR-14 IR-14 ID-11 I′-141 IR-15 IR-15 ID-11 I′-142 IR-16 IR-16 ID-11 I′-143 IR-21 IR-21 ID-11 I′-144 IR-22 IR-22 ID-11 I′-145 IR-23 IR-23 ID-11 I′-146 IR-24 IR-24 ID-11 I′-147 IR-25 IR-25 ID-11 I′-148 IR-26 IR-26 ID-11 I′-149 IR-27 IR-27 ID-11 I′-150 IR-28 IR-28 ID-11 I′-151 IR-29 IR-29 ID-11 I′-152 IR-30 IR-30 ID-11 I′-153 IR-31 IR-31 ID-11 I′-154 IR-32 IR-32 ID-11 I′-155 IR-33 IR-33 ID-11 I′-156 IR-34 IR-34 ID-11 I′-157 IR-35 IR-35 ID-11 I′-158 IR-36 IR-36 ID-11 I′-159 IR-37 IR-37 ID-11 I′-160 IR-38 IR-38 ID-11

TABLE 23 Ring formed with Salt R^(1A), R^(2A) and N Cation I′-201 IR-301 ID-11 I′-202 IR-302 ID-11 I′-203 IR-303 ID-11 I′-204 IR-304 ID-11 I′-205 IR-305 ID-11 I′-206 IR-306 ID-11 I′-207 IR-307 ID-11 I′-208 IR-308 ID-11 I′-209 IR-309 ID-11 I′-210 IR-310 ID-11 I′-211 IR-311 ID-11 I′-212 IR-312 ID-11 I′-213 IR-313 ID-11 I′-214 IR-314 ID-11 I′-215 IR-315 ID-11 I′-216 IR-316 ID-11 I′-217 IR-317 ID-11 I′-218 IR-318 ID-11 I′-219 IR-319 ID-11 I′-220 IR-320 ID-11 I′-221 IR-321 ID-11 I′-222 IR-322 ID-11 I′-223 IR-323 ID-11 I′-224 IR-324 ID-11 I′-225 IR-325 ID-11 I′-226 IR-326 ID-11 I′-227 IR-327 ID-11 I′-228 IR-328 ID-11 I′-229 IR-329 ID-11

TABLE 24 Salt R^(1A) R^(2A) Cation I′-301 IR-30 H ID-1 I′-302 IR-30 H ID-2 I′-303 IR-30 H ID-3 I′-304 IR-30 H ID-4 I′-305 IR-30 H ID-5 I′-306 IR-30 H ID-6 I′-307 IR-30 H ID-7 I′-308 IR-30 H ID-8 I′-309 IR-30 H ID-9 I′-310 IR-30 H ID-10 I′-311 IR-30 H ID-12 I′-312 IR-30 H ID-13 I′-313 IR-30 H ID-14 I′-314 IR-30 IR-1 ID-1 I′-315 IR-30 IR-1 ID-9 I′-316 IR-30 IR-1 ID-10 I′-317 IR-30 IR-2 ID-1 I′-318 IR-30 IR-2 ID-9 I′-319 IR-30 IR-2 ID-10 I′-320 IR-30 IR-3 ID-1 I′-321 IR-30 IR-3 ID-9 I′-322 IR-30 IR-3 ID-10 I′-323 IR-30 IR-4 ID-1 I′-324 IR-30 IR-4 ID-9 I′-325 IR-30 IR-4 ID-10 I′-326 IR-30 IR-5 ID-1 I′-327 IR-30 IR-5 ID-9 I′-328 IR-30 IR-5 ID-10 I′-329 IR-30 IR-6 ID-1 I′-330 IR-30 IR-6 ID-9 I′-331 IR-30 IR-6 ID-10 I′-332 IR-30 IR-7 ID-1 I′-333 IR-30 IR-7 ID-9 I′-334 IR-30 IR-7 ID-10

TABLE 25 Ring formed with Salt R^(1A), R^(2A) and N Cation I′-401 IR-305 ID-1 I′-402 IR-305 ID-9 I′-403 IR-306 ID-1 I′-404 IR-306 ID-9 I′-405 IR-314 ID-1 I′-406 IR-314 ID-9 I′-407 IR-315 ID-1 I′-408 IR-315 ID-9 I′-409 IR-316 ID-1 I′-410 IR-316 ID-2 I′-411 IR-316 ID-3 I′-412 IR-316 ID-4 I′-413 IR-316 ID-5 I′-414 IR-316 ID-6 I′-415 IR-316 ID-7 I′-416 IR-316 ID-8 I′-417 IR-316 ID-9 I′-418 IR-316 ID-10 I′-419 IR-316 ID-12 I′-420 IR-316 ID-13 I′-421 IR-316 ID-14 I′-422 IR-326 ID-1 I′-423 IR-326 ID-9 I′-424 IR-327 ID-1 I′-425 IR-327 ID-9 I′-426 IR-328 ID-1 I′-427 IR-328 IB-9

Among these, the salts represented by the formulae (I-19), (I-29), (I-78), (I-150), (I-151), (I-205), (I-206), (I-214), (I-216), (I-301), (I-305), (I-313), (I-317), (I-321), (I-325), (I-329), (I-333), (I-337), (I-341), (I-345), (I-349), (I-401), (I-405), (I-409), (I-410) are preferable, and the salts represented by the formulae (I-151), (I-216), (I-309), (I-313), (I-366), (I-349), (I-401), (I-409), (I-414), (I-417), (I-420) are more preferable. Also, the salts represented by the formulae (I′-1), (I′-2), (I′-216), (I′-228), (I′-301), (I′-305), (I′-409) are preferable, and the salts represented by the formulae (I′-1) and (I′-216) are more preferable.

(1) The sulfonium salt having the anion represented by the formula (IA) and the cation represented by the formula (IB) can be produced by the method described below.

A salt represented by the formula (IA-R2) can be produced by reacting an amine represented by the formula (IA-R1) with a sulfur-containing compound selected from chlorosulfuric acid, sulfuric ion or sulfur trioxide in a solvent under basic condition.

The sulfonium salt having the anion represented by the formula (IA) and the sulfonium salt having sulfonium cation represented by the formula (IB) can be produced by reacting the obtained salt represented by the formula (IA-R2) with a salt represented by the formula (IB-R1) in a solvent. Preferred examples of the solvent include organic solvent such as chloroform, dichloroethane, dichloromethane, acetonitrile, dimethyl formamide and tetrahydrofuran. Preferred examples of the base include triethylamine, DBU, dimethylamino pyridine and Pyridine.

wherein X^(A1+) represents an ammonium cation;

X^(B1+) represents halogen anion selected from Cl, Br, I, or an alkyl sulphate ion, a sulphate ion, a carboxylate anion, an alkoxy anion, or a hydroxide ion.

(2) A sulfonium salt having an anion represented by the formula (1A) and a cation represented by the formula (ID) can be produced by the method described below.

A salt represented by the formula (IA-R2) can be produced by reacting an amine represented by the formula (IA-R1) with a sulfur-containing compound selected from chlorosulfuric acid, sulfuric ion or sulfur trioxide in a solvent under basic condition.

The sulfonium salt having an anion represented by the formula (IA) and a cation represented by the formula (ID) can be produced by stirring the obtained salt represented by the formula (IA-R2) and a salt represented by the formula (ID-R1) in a solvent. Preferred examples of the solvent include organic solvent such as chloroform, dichloroethane, dichloromethane, acetonitrile, dimethyl formamide and tetrahydrofuran. Preferred examples of the base include triethylamine, DBU, dimethylamino pyridine and pyridine

wherein X^(A1+) and X^(B1+) represent the same meaning as described above.

The sulfonium salt having the anion represented by the formula (IA) contains preferably 0.01 to 1.5 parts by weight, and more preferably 0.02 to 0.5 parts by weight, with respect to 10 parts by weight of the resin (A) in the resist composition.

<Solvent (E)>

The resist composition of the present invention may include a solvent (E) in the amount of 90 weight % or more, preferably 92 weight % or more, and more preferably 94 weight % or more, and 99.9 weight % or less, preferably 99 weight % or less in the composition.

The content of the solvent (E) can be measured with a known analytical method such as, for example, liquid chromatography and gas chromatography.

Examples of the solvent (E) include glycol ether esters such as ethylcellosolve acetate, methylcellosolve acetate and propylene glycol monomethyl ether acetate; glycol ethers such as propylene glycol monomethyl ether; ethers such as diethylene glycol dimethyl ether; esters such as ethyl lactate, butyl acetate, amyl acetate and ethyl pyruvate; ketones such as acetone, methyl isobutyl ketone, 2-heptanone and cyclohexanone; and cyclic esters such as γ-butyrolactone. These solvents may be used as a single solvent or as a mixture of two or more solvents.

<Basic Compound (C)>

The resist composition of the present invention may contain a basic compound (C). The basic compound (C) is a compound having a property to quench an acid, in particular, generated from the acid generator (B), and called “quencher”.

As the basic compounds (C), nitrogen-containing basic compounds (for example, amine and basic ammonium salt) are preferable. The amine may be an aliphatic amine or an aromatic amine. The aliphatic amine includes any of a primary amine, secondary amine and tertiary amine. The aromatic amine includes an amine in which an amino group is bonded to an aromatic ring such as aniline, and a hetero-aromatic amine such as pyridine.

Preferred basic compounds (C) include compounds presented by the formula (C1) to the formula (C8) as described below. Among these, the basic compound presented by the formula (C1-1) is more preferable.

wherein R^(c1), R^(c2) and R^(c3) independently represent a hydrogen atom, a C₁ to C₆ alkyl group, C₅ to C₁₀ alicyclic hydrocarbon group or a C₆ to C₁₀ aromatic hydrocarbon group, one or more hydrogen atom contained in the alkyl group and alicyclic hydrocarbon group may be replaced by a hydroxy group, an amino group or a C₁ to C₆ alkoxyl group, one or more hydrogen atom contained in the aromatic hydrocarbon group may be replaced by a C₁ to C₆ alkyl group, a C₁ to C₆ alkoxyl group, a C₅ to C₁₀ alicyclic hydrocarbon group or a C₆ to C₁₀ aromatic hydrocarbon group.

wherein R^(c2) and R^(c3) have the same definition of the above;

R^(c4) in each occurrence represents a C₁ to C₆ alkyl group, a C₁ to C₆ alkoxyl group, a C₅ to C₁₀ alicyclic hydrocarbon group or a C₆ to C₁₀ aromatic hydrocarbon group;

m3 represents an integer 0 to 3.

wherein R^(c5), R^(c6), R^(c7) and R^(c8) independently represent the any of the group as described in R^(c1) of the above;

R^(c9) in each occurrence independently represents a C₁ to C₆ alkyl group, a C₃ to C₆ alicyclic hydrocarbon group or a C₂ to C₆ alkanoyl group;

n3 represents an integer of 0 to 8.

Examples of the alkanoyl group include acetyl group, 2-methylacetyl group, 2,2-dimethylacetyl group, propionyl group, butylyl group, isobutylyl group, pentanoyl group, and 2,2-dimethylpropionyl group.

wherein R^(c10), R^(c11), R^(c12), R^(c13) and R^(c16) independently represent the any of the groups as described in R^(c1);

R^(c14), R^(c15) and R^(c17) in each occurrence independently represent the any of the groups as described in R^(c4);

o3 and p3 represent an integer of 0 to 3;

L^(c1) represents a divalent C₁ to C₆ alkanediyl group, —CO—, —C(═NH)—, —S— or a combination thereof.

wherein R^(c18), R^(c19) and R^(c20) in each occurrence independently represent the any of the groups as described in R^(c4);

q3, r3 and s3 represent an integer of 0 to 3;

L^(c2) represents a single bond, a C₁ to C₆ alkanediyl group, —CO—, —C(═NH)—, —S— or a combination thereof.

Specific examples of the amine represented by the formula (C1) include 1-naphtylamine and 2-naphtylamine, aniline, diisopropylaniline, 2-, 3- or 4-methylaniline, 4-nitroaniline, N-methylaniline, N,N-dimethylaniline, diphenylamine, hexylamine, heptylamine, octylamine, nonylamine, decylamine, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, triethylamine, trimethylamine, tripropylamine, tributylamine, tripentylamine, trihexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, methyldibutylamine, methyldipentylamine, methyldihexylamine, methyldicyclohexylamine, methyldiheptylamine, methyldioctylamine, methyldinonylamine, methyldidecylamine, ethyldibutylamine, ethyldipentylamine, ethyldihexylamine, ethyldiheptylamine, ethyldioctylamine, ethyldinonylamine, ethyldidecylamine, dicyclohexylmethylamine, tris[2-(2-methoxyethoxy)ethyl]amine, triisopropanolamine, ethylene diamine, tetramethylene diamine, hexamethylene diamine, 4,4′-diamino-1,2-diphenylethane, 4,4′-diamino-3,3′-dimethyldiphenylmethane and 4,4′-diamino-3,3′-diethyldiphenylmethane.

Among these, diisopropylaniline is preferable, particularly 2,6-diisopropylaniline is more preferable as the basic compounds (C) contained in the present resist composition.

Specific examples of the compound represented by the formula (C2) include, for example, piperadine.

Specific examples of the compound represented by the formula (C3) include, for example, morpholine.

Specific examples of the compound represented by the formula (C4) include, for example, piperidine, a hindered amine compound having piperidine skeleton described in JP H11-52575-A.

Specific examples of the compound represented by the formula (C5) include, for example, 2,2′-methylenebisaniline.

Specific examples of the compound represented by the formula (C6) include, for example, imidazole and 4-methylimidazole.

Specific examples of the compound represented by the formula (C7) include, for example, pyridine and 4-methylpyrizine.

Specific examples of the compound represented by the formula (C8) include, for example, 1,2-di(2-pyridyl)ethane, 1,2-di(4-pyridyl)ethane, 1,2-di(2-pyridyl)ethene, 1,2-di(4-pyridyl)ethene, 1,3-di(4-pyridyl)propane, 1,2-di(4-pyridyloxy)ethane, di(2-pyridyl)ketone, 4,4′-dipyridyl sulfide, 4,4′-dipyridyl disulfide, 2,2′-dipyridylamine, 2,2′-dipicolylamine and bipyridine.

Examples of the ammonium salt include tetramethylammonium hydroxide, tetraisopropylammonium hydroxide, tetrabutylammonium hydroxide, tetrahexylammonium hydroxide, tetraoctylammonium hydroxide, phenyltrimethyl ammonium hydroxide, 3-(trifluoromethyl)phenyltrimethylammonium hydroxide, tetra-n-butyl ammonium salicylate and choline.

The proportion of the basic compound (C) is preferably 0.01 to 5 weight %, more preferably 0.01 to 3 weight %, and still more preferably 0.01 to 1 weight % with respect to the total solid proportion of the resist composition.

<Other Ingredient (Hereinafter May be Referred to as “Other Ingredient (F)”>

The resist composition can also include small amounts of various additives such as sensitizers, dissolution inhibitors, surfactants, stabilizers, and dyes, as needed.

<Preparing the Resist Composition>

The present resist composition can be prepared by mixing the resin (A), the acid generator (B) and the salt having anion represented by the formula (IA), and the basic compound (C), the solvent (E) and the other ingredient (F) as needed. There is no particular limitation on the order of mixing. The mixing may be performed in an arbitrary order. The temperature of mixing may be adjusted to an appropriate temperature within the range of 10 to 40° C., depending on the kinds of the resin and solubility in the solvent (E) of the resin. The time of mixing may be adjusted to an appropriate time within the range of 0.5 to 24 hours, depending on the mixing temperature. There is no particular limitation to the tool for mixing. An agitation mixing may be adopted.

After mixing the above ingredients, the present resist compositions can be prepared by filtering the mixture through a filter having about 0.003 to 0.2 μm pore diameter.

<Method for Producing Resist Pattern>

The method for producing resist pattern of the present invention includes the steps of:

(1) applying the resist composition of the present invention onto a substrate;

(2) drying the applied composition to form a composition layer;

(3) exposing the composition layer;

(4) heating the exposed composition layer, and

(5) developing the heated composition layer.

Applying the resist composition onto the substrate can generally be carried out through the use of a resist application device, such as a spin coater known in the field of semiconductor microfabrication technique. The thickness of the applied resist composition layer can be adjusted by controlling the variable conditions of the resist application device. These conditions can be selected based on a pre-experiment carried out beforehand. The substrate can be selected from various substrates intended to be microfabricated. The substrate may be washed, and an organic antireflection film may be formed on the substrate by use of a commercially available antireflection composition, before the application of the resist composition.

Drying the applied composition layer, for example, can be carried out using a heating device such as a hotplate (so-called “prebake”), a decompression device, or a combination thereof. Thus, the solvent evaporates from the resist composition and a composition layer with the solvent removed is formed. The condition of the heating device or the decompression device can be adjusted depending on the kinds of the solvent used. The temperature in this case is generally within the range of 50 to 200° C. Moreover, the pressure is generally within the range of 1 to 1.0×10⁵ Pa.

The composition layer thus obtained is generally exposed using an exposure apparatus or a liquid immersion exposure apparatus. The exposure is generally carried out through a mask that corresponds to the desired pattern. Various types of exposure light source can be used, such as irradiation with ultraviolet lasers such as KrF excimer laser (wavelength: 248 nm), ArF excimer laser (wavelength: 193 nm), F₂ excimer laser (wavelength: 157 nm), or irradiation with far-ultraviolet wavelength-converted laser light from a solid-state laser source (YAG or semiconductor laser or the like), or vacuum ultraviolet harmonic laser light or the like. Also, the exposure device may be one which irradiates electron beam or extreme-ultraviolet light (EUV).

After exposure, the composition layer is subjected to a heat treatment (so-called “post-exposure bake”) to promote the deprotection reaction. The heat treatment can be carried out using a heating device such as a hotplate. The heating temperature is generally in the range of 50 to 200° C., preferably in the range of 70 to 150° C.

The composition layer is developed after the heat treatment, generally with an alkaline developing solution and using a developing apparatus. The development here means to bring the composition layer after the heat treatment into contact with an alkaline solution. Thus, the exposed portion of the composition layer is dissolved by the alkaline solution and removed, and the unexposed portion of the composition layer remains on the substrate, whereby producing a resist pattern. Here, as the alkaline developing solution, various types of aqueous alkaline solutions used in this field can be used. Examples include aqueous solutions of tetramethylammonium hydroxide and (2-hydroxyethyl)trimethylammonium hydroxide (common name: choline).

After the development, it is preferable to rinse the substrate and the pattern with ultrapure water and to remove any residual water thereon.

<Application>

The resist composition of the present invention is useful as the resist composition for excimer laser lithography such as with ArF, KrF or the like, and the resist composition for electron beam (EB) exposure lithography and extreme-ultraviolet (EUV) exposure lithography, as well as liquid immersion exposure lithography.

The resist composition of the present invention can be used in semiconductor microfabrication and in manufacture of liquid crystals, thermal print heads for circuit boards and the like, and furthermore in other photofabrication processes, which can be suitably used in a wide range of applications.

EXAMPLES

The present invention will be described more specifically by way of examples, which are not construed to limit the scope of the present invention.

All percentages and parts expressing the content or amounts used in the Examples and Comparative Examples are based on weight, unless otherwise specified.

The composition ratio of the resin (the copolymerization ratio of the structural unit derived from each monomer used in the preparation with respect to the resin) was calculated by measuring the amount of the unreacted monomer in the reacted solution after the completion of the reaction through liquid chromatography, and calculating the amount of the monomer use in the polymerization from the obtained results.

The weight average molecular weight is a value determined by gel permeation chromatography.

Column: TSK gel Multipore HXL-M×3+guardcolumn (Tosoh Co. Ltd.)

Eluant: tetrahydrofuran

Flow rate: 1.0 mL/min

Detecting device: RI detector

Column temperature: 40° C.

Injection amount: 100 μL

Standard material for calculating molecular weight: standard polysthylene (Toso Co. ltd.)

Synthesis Example 1 Synthesis of a Salt (I-409)

To a solution of 1.7 parts of a compound represented by the formula (I-409-b) (obtained from Tokyo Chemical Industry Co., LTD) and 50.00 parts of chloroform, 2.8 parts of trimethyl amine was added, cooled to −10° C., and 1.6 parts of a compound represented by the formula (I-409-c) was added thereto. After that, the obtained mixture was stirred for 1 hour at room temperature. To the reacted mixture, a salt represented by the formula (I-409-d) was added, and stirred over one night. 20 parts of ion-exchanged water was added to the obtained mixture, and the obtained mixture was extracted by chloroform. The chloroform solution was vacuum-concentrated, a mixture solution of acetonitrile and 2-methoxy-2-methylpropane was added thereto, and removed a supernatant by decantation. The obtained residue was dried, whereby giving 5.4 parts of a salt represented by the formula (I-409).

MS (ESI(+) Spectrum): M⁺ 305.1 (C₂₁H₂₁S⁺=305.1)

MS (ESI(−) Spectrum): M⁻ 218.1 (C₉H₁₆NO₃S⁻=218.1)

Synthesis Example 2 Synthesis of a Salt (I-401)

To a solution of 5.0 parts of a compound represented by the formula (I-401-a) (obtained from Tokyo Chemical Industry Co., LTD), 5.0 parts of chloroform and 35 parts of ion-exchanged water, 7.43 parts of a compound represented by the formula (I-401-b) was added, and stirred for 4 hours at room temperature. A water layer of the reacted mixture was removes, and washed an obtained organic layer with ion-exchanged water. The obtained organic layer was vacuum-concentrated, a mixture solution of acetonitrile and 2-methoxy-2-methylpropane was added thereto, and removed a supernatant by decantation. The obtained residue was dried, whereby giving 3.4 parts of a salt represented by the formula (I-401).

MS (ESI(+) Spectrum): M⁺ 263.1 (C₁₈H₁₅S⁺=263.1)

MS (ESI(−) Spectrum): M⁻ 181.1 (C₆H₁₂NO₃S⁻=181.1)

Synthesis Example 3 Synthesis of Compound Represented by the Formula (K)

10.00 parts of a compound (K-2), 40.00 parts of tetrahydrofuran and 7.29 parts of pyridine were mixed, and stirred for 30 minutes at 23° C. The obtained mixture was cooled to 0° C. To this mixture was added 33.08 parts of a compound (K-1) over 1 hour while maintaining at the same temperature. The temperature of the mixture was then elevated to about 23° C., and the mixture was stirred for 3 hours at the same temperature. Thus obtained reactant was added to 361.51 parts of ethyl acetate and 20.19 parts of 5% of hydrochloric acid solution to obtain a mixture, the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. To the recovered organic layer, 81.42 parts of a saturated sodium hydrogen carbonate was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to recover the organic layer. To the recovered organic layer was added 90.38 parts of ion-exchanged water, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to wash the organic layer with water. These washing operations were repeated for 5 times. The obtained organic layer was concentrated, whereby giving 23.40 parts of the compound (K).

MS (mass spectroscopy): 326.0 (molecular peak)

Synthesis Example 4 Synthesis of Compound Represented by the Formula (H)

88.00 parts of a compound (H-2), 616.00 parts of methyl isobutyl ketone and 60.98 parts of pyridine were mixed, and stirred for 30 minutes at 23° C. The obtained mixture was cooled to 0° C. To this mixture was added 199.17 parts of a compound (H-1) over 1 hour while maintaining at the same temperature. The temperature of the mixture was then elevated to about 10° C., and the mixture was stirred for 1 hour at the same temperature. Thus obtained reactant was added to 1446.22 parts of n-heptane and 703.41 parts of 2% of hydrochloric acid solution to obtain a mixture, the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. To the recovered organic layer, 337.64 parts of 2% of hydrochloric acid solution was added to obtain a mixture, and the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. To the recovered organic layer, 361.56 parts of ion-exchanged water was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to wash the organic layer with water. To the obtained organic layer, 443.92 parts of 10% of potassium carbonate was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to recover the organic layer. These washing operations were repeated for 2 times. To the obtained organic layer, 361.56 parts of ion-exchanged water was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to wash the organic layer with water. These washing operations were repeated for 5 times. The obtained organic layer was concentrated, whereby giving 163.65 parts of the compound (H).

MS (mass spectroscopy): 276.0 (molecular ion peak)

Synthesis Example 5 Synthesis of Compound Represented by the Formula (L)

30.00 parts of a compound (L-2), 210.00 parts of methyl isobutyl ketone and 18.00 parts of pyridine were mixed, and stirred for 30 minutes at 23° C. The obtained mixture was cooled to 0° C. To this mixture was added 48.50 parts of a compound (L-1) over 1 hour while maintaining at the same temperature. The temperature of the mixture was then elevated to about 5° C., and the mixture was stirred for 1 hour at the same temperature. Thus obtained reactant was added to 630 parts of ethyl acetate, 99.68 parts of 5% of hydrochloric acid solution and 126 parts of ion-exchanged water to obtain a mixture, the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. To the recovered organic layer, 86.50 parts of 10% of potassium carbonate solution was added to obtain a mixture, and the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. These washing operations were repeated for two times. To the recovered organic layer, 157.50 parts of ion-exchanged water was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to wash the organic layer with water. These washing operations were repeated for five times. The obtained organic layer was concentrated, whereby giving 27.61 parts of the compound (L).

MS (mass spectroscopy): 3541 (molecular ion peak)

Synthesis Example 6 Synthesis of Compound Represented by the Formula (M)

27.34 parts of a compound (M-2), 190.00 parts of methyl isobutyl ketone and 18.00 parts of pyridine were mixed, and stirred for 30 minutes at 23° C. The obtained mixture was cooled to 0° C. To this mixture was added 48.50 parts of a compound (M-1) over 1 hour while maintaining at the same temperature. The temperature of the mixture was then elevated to about 5° C., and the mixture was stirred for 1 hour at the same temperature. Thus obtained reactant was added to 570 parts of ethyl acetate, 99.68 parts of 5% of hydrochloric acid solution and 126 parts of ion-exchanged water to obtain a mixture, the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. To the recovered organic layer, 86.50 parts of 10% of potassium carbonate solution was added to obtain a mixture, and the mixture was stirred for 30 minutes at 23° C. The obtained solution was allowed to stand, and then separated to recover an organic layer. These washing operations were repeated for two times. To the recovered organic layer, 150 parts of ion-exchanged water was added, and the obtained solution was stirred for 30 minutes at 23° C., allowed to stand, and then separated to wash the organic layer with water. These washing operations were repeated for five times. The obtained organic layer was concentrated, whereby giving 23.89 parts of the compound (M).

MS (mass spectroscopy): 340.1 (molecular ion peak)

Synthetic Example of the Resin

The monomers used the synthesis of the resin are shown below.

Synthetic Example 7 Synthesis of Resin A1-1

Monomer (H) was used, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 0.7 mol % and 2.1 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a large amount of methanol/water mixed solvent to precipitate a resin. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol/water mixed solvent to precipitate a resin. The obtained resin was filtrated. These operations were repeated for two times, resulting in a 77% yield of copolymer having a weight average molecular weight of about 18000. This copolymer, which had the structural units of the following formula, was referred to Resin A1-1.

Synthetic Example 8 Synthesis of Resin A1-2

Monomer (K) and monomer (I) were mixed together with a mole ratio of Monomer (K):monomer (I)=90:10, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1 mol % and 3 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 72° C. After that, the obtained reacted mixture was poured into a large amount of n-heptane to precipitate a resin. The obtained resin was filtrated, resulting in a 70% yield of copolymer having a weight average molecular weight of about 13000. This copolymer, which had the structural units of the following formula, was referred to

Resin A1-2.

Synthetic Example 9 Synthesis of Resin A1-3

Monomer (L) was used, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 0.7 mol % and 2.1 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a large amount of methanol/water mixed solvent to precipitate a resin. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol/water mixed solvent to precipitate a resin. The obtained resin was filtrated. These operations were repeated for two times, resulting in a 73% yield of copolymer having a weight average molecular weight of about 19000. This copolymer, which had the structural units of the following formula, was referred to Resin A1-3.

Synthetic Example 10 Synthesis of Resin A1-4

Monomer (M) was used, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 0.7 mol % and 2.1 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a large amount of methanol/water mixed solvent to precipitate a resin. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol/water mixed solvent to precipitate a resin. The obtained resin was filtrated. These operations were repeated for two times, resulting in a 76% yield of copolymer having a weight average molecular weight of about 18000. This copolymer, which had the structural units of the following formula, was referred to Resin A1-4.

Synthetic Example 11 Synthesis of Resin A2-1

Monomer (D), monomer (E), monomer (B), monomer (C) and monomer (F) were mixed together with a mole ratio of monomer (D):monomer (E):monomer (B):monomer (C):monomer (F)=30:14:6:20:30, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1.0 mol % and 3.0 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water (methanol: water=4:1, weight ratio) to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a large amount of a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated two times, resulting in a 65% yield of copolymer having a weight average molecular weight of about 8100. This copolymer, which had the structural units of the following formula, was referred to Resin A2-1.

Synthetic Example 12 Synthesis of Resin A2-2

Monomer (A), monomer (E), monomer (B), monomer (C) and monomer (F) were mixed together with a mole ratio of monomer (A):monomer (E):monomer (B):monomer (C):monomer (F)=30:14:6:20:30, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1.0 mol % and 3.0 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 73° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water (methanol: water=4:1, weight ratio) to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a large amount of a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated two times, resulting in a 68% yield of copolymer having a weight average molecular weight of about 7800. This copolymer, which had the structural units of the following formula, was referred to Resin A2-2.

Synthetic Example 13 Synthesis of Resin A2-3

Monomer (A), monomer (B) and monomer (C) were mixed together with a mole ratio of monomer (A):monomer (B):monomer (C)=50:25:25, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1.0 mol % and 3.0 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 8 hours at 80° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water (methanol: water=4:1, weight ratio) to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated three times, resulting in a 60% yield of copolymer having a weight average molecular weight of about 9200. This copolymer, which had the structural units of the following formula, was referred to Resin A2-3.

Synthetic Example 14 Synthesis of Resin A2-4

Monomer (A), monomer (E), monomer (B), monomer (F) and monomer (C) were mixed together with a mole ratio of monomer (A):monomer (E):monomer (B):monomer (F):monomer (C)=30:14:6:20:30, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1 mol % and 3 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a large amount of a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated two times, resulting in a 78% yield of copolymer having a weight average molecular weight of about 7200. This copolymer, which had the structural units of the following formula, was referred to Resin A2-4.

Synthetic Example 15 Synthesis of Resin A2-5

Monomer (A), monomer (N), monomer (B), monomer (F) and monomer (C) were mixed together with a mole ratio of monomer (A): monomer (N):monomer (B):monomer (F):monomer (C)=30:14:6:20:30, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1 mol % and 3 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a large amount of a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated two times, resulting in a 78% yield of copolymer having a weight average molecular weight of about 7200. This copolymer, which had the structural units of the following formula, was referred to Resin A2-5.

Synthetic Example 16 Synthesis of Resin X1

Monomer (G), monomer (C) and monomer (B) were mixed together with a mole ratio of monomer (G):monomer (C):monomer (B)=35:45:20, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 1.0 mol % and 3.0 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 75° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol and water to precipitate a resin. The obtained resin was filtrated. These operations were repeated 2 times, resulting in a 75% yield of copolymer having a weight average molecular weight of about 7000. This copolymer, which had the structural units of the following formula, was referred to Resin X1. The mole ratio of each structural unit is structural unit (G): structural unit (C): structural unit (B)=34.7:45.4:19.9.

Synthetic Example 17 Synthesis of Resin X2

Monomer (J) and monomer (G) were mixed together with a mole ratio of monomer (J):monomer (G)=80:20, and dioxane was added thereto in an amount equal to 1.5 times by weight of the total amount of monomers to obtain a solution. Azobisisobutyronitrile and azobis(2,4-dimethylvaleronitrile) was added as an initiator to obtain a solution in an amount of 0.5 mol % and 1.5 mol % respectively with respect to the entire amount of monomers, and the resultant mixture was heated for about 5 hours at 70° C. After that, the obtained reacted mixture was poured into a mixture of a large amount of methanol and water to precipitate a resin. The obtained resin was filtrated. Thus obtained resin was dissolved in another dioxane to obtain a solution, and the solution was poured into a mixture of methanol and ion-exchanged water to precipitate a resin. The obtained resin was filtrated. These operations were repeated 2 times, resulting in a 70% yield of copolymer having a weight average molecular weight of about 28000. This copolymer, which had the structural units of the following formula, was referred to Resin X2. The mole ratio of each structural unit is structural unit (j): structural unit (G)=80.2:19.8.

(Preparing Resist Composition)

Resist compositions were prepared by mixing and dissolving each of the components shown in Table 26, and then filtrating through a fluororesin filter having 0.2 μm pore diameter.

TABLE 1 (Unit: parts) Resin Acid Generator Compound (IA) PB/PEB(° C./° C.) Ex. 1 A1-1/A2-1 = 0.7/10 B1 = 1.0 D1 = 0.04 95/85 2 A1-1/A2-2 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 3 A1-2/A2-1 = 0.3/10 B1 = 1.0 D1 = 0.04 95/85 4 A1-2/A2-2 = 0.3/10 B1 = 1.0 D1 = 0.04 110/105 5 A1-1/A2-3 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 6 A1-1/A2-1 = 0.7/10 B1 = 1.0 D2 = 0.04 95/85 7 A1-1/X1 = 0.7/10 B2/B3 = 1.0/0.1 D1 = 0.03 120/115 8 A1-1/A2-4 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 9 A1-1/A2-5 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 10 A1-3/A2-5 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 11 A1-4/A2-5 = 0.7/10 B1 = 1.0 D1 = 0.04 110/105 Comparative Example 1 X2/X1 = 0.3/10 B2/B3-1.0/0.1 — 120/115

<Resin>

Resin prepared by the Synthetic Examples

<Acid Generator>

B1: this was prepared by a method according to the method described in the Examples of JP2010-152341A

B2: this was prepared by a method according to the method described in the Examples of WO2008/99869A and JP2010-26478A

B3: this was prepared by a method according to the method described in the Examples of JP2005-221721A

<Salt Having Anion Represented by the Formula (IA)>

D1 (compound (I-409)):

D1 (compound (I-401)):

<Solvent of Resist Composition>

Propylene glycol monomethyl ether acetate 265 parts Propylene glycol monomethyl ether 20 parts 2-Heptanone 20 parts γ-butyrolactone 3.5 parts

(Producing Resist Pattern)

A composition for an organic antireflective film (“ARC-29”, by Nissan Chemical Co. Ltd.) was applied onto silicon wafers and baked for 60 seconds at 205° C. to form a 78 nm thick organic antireflective film on each of the silicon wafers.

The above resist compositions were then applied thereon by spin coating so that the thickness of the resulting composition layer became 85 nm after drying.

The obtained wafers were then pre-baked for 60 seconds on a direct hot plate at the temperatures given in the “PB” column in Table 26 to form a composition layer.

Line and space patterns were then exposed using a mask pattern through stepwise changes in exposure quantity using an ArF excimer laser stepper for immersion lithography (“XT:1900Gi” by ASML Ltd.: NA=1.35, 3/42 annular X-Y polarization), on the wafers on which the composition layer had thus been formed. The ultrapure water was used as medium of immersion.

After the exposure, post-exposure baking was carried out for 60 seconds at the temperatures given in the “PEB” column in Table 26.

Then, puddle development was carried out with 2.38 wt % tetramethylammonium hydroxide aqueous solution for 60 seconds to obtain resist patterns.

Effective sensitivity was represented as the exposure amount at which a 50 nm line and space pattern resolved to 1:1 with the each resist film.

(Focus Margin (DOF) Evaluation)

For the effective sensitivity, when the focus fluctuated with a standard width as the range with a line width of 50 nm±5% (47.5 to 52.5 nm),

a “oo” was given when the DOF value was >0.18 μm,

a “o” was given when the DOF value was >0.12 μm, ≦0.18 μm and

an “x” was given when the DOF value was ≦0.12 μm.

Table 27 illustrates the results thereof. The parenthetical number means DOF values.

(Evaluation of Defects)

The above resist compositions were applied on each of the 12-inch-silicon wafers by spin coating so that the thickness of the resulting film became 150 nm after drying.

The obtained wafers were then pre-baked for 60 seconds on a direct hot plate at the temperatures given in the “PB” column in Table 26 to obtain a composition layer.

The thus obtained wafers with the produced composition layers are rinsed with water for 60 seconds using a developing apparatus (ACT-12, Tokyo electron Co. Ltd.).

Thereafter, the number of defects was counted using a defect inspection apparatus (KLA-2360, KLA-Tencor Co. Ltd.)

Table 27 illustrates the results thereof.

TABLE 27 DOF Defects Ex. 1 ◯◯ (0.21) 180 2 ◯◯ (0.24) 190 3 ◯ (0.18) 220 4 ◯◯ (0.21) 230 5 ◯ (0.15) 410 6 ◯◯ (0.21) 200 7 ◯ (0.15) 290 8 ◯◯ (0.24) 150 9 ◯◯ (0.24) 130 10 ◯◯ (0.21) 100 11 ◯◯ (0.21) 120 Comp. Ex. 1 X (0.09) 720

According to the resist composition of the present invention, it is possible to achieve satisfactory wide focus margin (DOF) and defect-free in the obtained resist pattern. Therefore, the present resist composition can be used for semiconductor microfabrication. 

1. A resist composition comprising; (A1) a resin having a structural unit represented by the formula (I), (A2) a resin being insoluble or poorly soluble in alkali aqueous solution, but becoming soluble in an alkali aqueous solution by the action of an acid, (B) an acid generator, and (D) a salt having an anion represented by the formula (IA),

wherein R¹ represents a hydrogen atom or a methyl group; A¹ represents a C₁ to C₆ alkanediyl group; R² represents a C₁ to C₁₀ hydrocarbon group having a fluorine atom,

wherein R^(1A) and R^(2A) independently represent a hydrogen atom, a C₁ to C₁₂ aliphatic hydrocarbon group, a C₃ to C₂₀ alicyclic hydrocarbon group, a C₆ to C₂₀ aromatic hydrocarbon group or a C₇ to C₂₁ aralkyl group, one or more hydrogen atom contained in the aliphatic hydrocarbon, the alicyclic hydrocarbon group, the aromatic hydrocarbon group and the aralkyl group may be replaced by a hydroxy group, a cyano group, a fluorine atom, a trifluoromethyl group or a nitro group, and one or more —CH₂— contained in the aliphatic hydrocarbon group may be replaced by —O— or —CO—, or R^(1A) and R^(2A) may be bonded together with a nitrogen atom bonded thereto to form a C₄ to C₂₀ ring.
 2. The resist composition according to claim 1, wherein R² in the formula (I) is a C₁ to C₆ fluorinated alkyl group.
 3. The resist composition according to claim 1, wherein A¹ in the formula (I) is a C₂ to C₄ alkanediyl group.
 4. The resist composition according to claim 1, wherein A¹ in the formula (I) is an ethylene group.
 5. The resist composition according to claim 1, wherein the salt having an anion represented by the formula (IA) contains a cation represented by the formula (IB),

wherein R³, R⁴ and R⁵ in each occurrence independently represent a hydroxy group, a halogen atom, a C₁ to C₁₂ alkyl group, a C₁ to C₁₂ alkoxy group or a C₃ to C₁₈ alicyclic hydrocarbon group, and the alkyl group, the alkoxy group and the alicyclic hydrocarbon group may be substituted with a halogen group, a hydroxy group, a C₁ to C₁₂ alkoxy group, a C₆ to C₁₈ aromatic hydrocarbon group, a C₂ to C₄ acyl group or a glycidyloxy group; mx to m/z independently represent an integer of 0 to
 5. 6. The resist composition according to claim 1, which further comprises a solvent.
 7. A method for producing resist pattern comprising steps of; (1) applying the resist composition of claim 1 onto a substrate; (2) drying the applied composition to form a composition layer; (3) exposing the composition layer; (4) heating the exposed composition layer, and (5) developing the heated composition layer. 